Plaster class III Stodent Ortho 25kg

Stodent III Ortho is a type 3 hard orthodontic plaster recommended for archival, diagnostic and working models when making removable orthodontic appliances.

Description:

• Glossy white color.
• Small expansion.

Advantages:

• Smooth surface.
• Easy to prepare and process.
• Surface resistance to abrasion.

Technical data:

• Mixing proportions approx. 28-30 ml / 100 g.
• Mixing time (vacuum) 30 s.
• Mixing time (manual) 60 – 90 s.
• Setting time 10 -14 min.
• Release time from the impression 45 min.
• Compressive resistance (after 1h ) 25 ± 2 MPa [> 20 MPa]
• Linear expansion (after 2 hours ) max. 0.15% [< 0.20 %]

Packaging:

• 25kg

Attention:

• Due to the heavy weight of the goods (25 kg), an additional fee will be added to the shipment.

Gypsum class III Stodent light green - mango scent 3kg

Stodent III is a type 3 hard plaster recommended for antagonist models and working models when making removable and skeletal dentures.

Description:

• Light green color enriched with mango aroma.
• Small expansion.
• Good mechanical properties.

Advantages:

• Smooth surface.
• Easier model making thanks to high thixotropy.
• High resistance to fracture when released from the impression.

Technical data:

• Mixing proportions 30 ml / 100 g.
• Mixing time (vacuum) 30 s.
• Mixing time (manual) 60 – 90 s.
• Setting time 10 -14 min.
• Release time from the impression 45 min.
• Compressive resistance (after 1h ) 25 ± 2 MPa [> 20 MPa]
• Linear expansion (after 2 hours ) max. 0.15% [< 0.20 %]

Packaging:

• 3kg.

Gypsum class III Stodent yellow 25kg

Stodent III is a type 3 hard plaster recommended for antagonist models and working models when making removable and skeletal dentures.

Description:

• Available in color: yellow.
• Small expansion.
• Good mechanical properties.

Advantages:

• Smooth surface.
• Easier model making thanks to high thixotropy.
• High resistance to fracture when released from the impression.

Technical data:

• Mixing proportions 30 ml / 100 g.
• Mixing time (vacuum) 30 s.
• Mixing time (manual) 60 – 90 s.
• Setting time 10 -14 min.
• Release time from the impression 45 min.
• Compressive resistance (after 1h ) 25 ± 2 MPa [> 20 MPa]
• Linear expansion (after 2 hours ) max. 0.15% [< 0.20 %]

Packaging:

• 25kg

Attention:

• Due to the heavy weight of the goods (25 kg), an additional fee will be added to the shipment.

Gypsum class III EcoStone yellow 5kg

Hard, high-quality type 3 synthetic plaster, intended for foundry work in the technique of partial dentures, frame dentures and orthodontic appliances. Meets the requirements of the ISO 6873-3 standard. Certificate of Admission No. IL-5629/MS.

Advantages:

• Obtaining models with high durability.
• Minimal, uniform expansion coefficient.
• Consistent level of quality.

Physical properties :

• Hardening time: approx. 10 min.
• Compressive strength after 1 h: over 20 N/mm2.
• Hardness after 24 hours over 80 N/mm2.
• Linear expansion after 2 hours : less than 0.14%.

Mixing proportions and method of use:

• Plaster 100 g: 30 ml.
• Water: gypsum 0.3 ml/g.
• Operating temperature approx. 23 °C.
• Fast in no more than 10 seconds. pour gypsum into water in the proportions given above.
• Wait 20 seconds. until the water is absorbed by the plaster.
• Mechanical mixing: 30 sec.
• Manual mixing: 60 sec.
• During this time, the plaster reaches the optimal consistency for pouring into model molds using a shaker.
• Shaking time: approx. 6 min.
• After this time, stop shaking so as not to disturb the crystallization process.

Storage :

• At least 12 months in a tight, moisture-proof packaging.

Packaging:

• 5kg.

Articulating plaster class III Quick-Rock 10kg

Quick-setting articulating plaster for mounting models in articulators with very good stability and minimal expansion.

Characteristic:

• White articulating plaster.

Parameters:

• Mixing proportions: 30 ml/ 100 g.
• Working time: 90 sec.
• Setting time: 3 min.
• Expansion after setting: 0.01%.
• Compressive strength 1h: 25 Mpa.

Packaging:

• 10kg. (5x2kg)

Gypsum class III EcoStone blue 5kg

Hard synthetic gypsum type 3, high quality, intended for casting work in the technique of partial dentures, frame dentures and orthodontic appliances. Meets the requirements of the ISO 6873-3 standard. Certificate of Admission No. IL-5629/MS.

Advantages:

• Highly durable models.
• Minimal, uniform expansion coefficient.
• Consistent level of quality.

Physical properties :

• Hardening time: approx. 10-12 minutes.
• Compressive strength after 1 h: over 20 N/mm2.
• Hardness after 24 hours over 80 N/mm2.
• Linear expansion after 2 hours : below 0.14%

Mixing proportions and method of use:

• Gypsum: water 100 g: 30 ml.
• Water: gypsum 0.3 ml/g.
• Operating temperature approx. 23° C.
• Fast in no more than 10 seconds. pour gypsum into water in the proportions given above and wait 20 seconds. until the water is absorbed by the plaster.
• Mechanical mixing: 30 sec.
• Manual mixing: 60 sec.
• During this time, the plaster reaches the optimal consistency for pouring into model molds using a shaker.
• Shaking time: approx. 6 min
• After this time, stop shaking so as not to disturb the crystallization process.

Storage :

• At least 12 months in a tight, moisture-proof packaging.

Packaging:

• 5kg.

Gypsum class III Stodent ORTHO white 5kg

Stodent III Ortho is a type 3 hard orthodontic plaster recommended for archival, diagnostic and working models when making removable orthodontic appliances.

Description:

• Glossy white color.
• Small expansion.

Advantages:

• Smooth surface.
• Easy to prepare and process.
• Surface resistance to abrasion.

Technical data:

• Mixing proportions approx. 28-30 ml / 100 g.
• Mixing time (vacuum) 30 s.
• Mixing time (manual) 60 – 90 s.
• Setting time 10 -14 min.
• Release time from the impression 45 min.
• Compressive resistance (after 1h ) 25 ± 2 MPa [> 20 MPa]
• Linear expansion (after 2 hours ) max. 0.15% [< 0.20 %]

Packaging:

• 5kg

Plaster class III Stodent yellow 5kg

Stodent III is a type 3 hard plaster recommended for antagonist models and working models when making removable and skeletal dentures.

Description:

• Available in color: yellow.
• Small expansion.
• Good mechanical properties.

Advantages:

• Smooth surface.
• Easier model making thanks to high thixotropy.
• High resistance to fracture when released from the impression.

Technical data:

• Mixing proportions 30 ml / 100 g.
• Mixing time (vacuum) 30 s.
• Mixing time (manual) 60 – 90 s.
• Setting time 10 -14 min.
• Release time from the impression 45 min.
• Compressive resistance (after 1h ) 25 ± 2 MPa [> 20 MPa]
• Linear expansion (after 2 hours ) max. 0.15% [< 0.20 %]

Packaging:

• 5kg

Gypsum class III Stodent light green - mango scent 5 kg

Stodent III is a type 3 hard plaster recommended for antagonist models and working models when making removable and skeletal dentures.

Description:

• Light green color enriched with mango aroma.
• Small expansion.
• Good mechanical properties.

Advantages:

• Smooth surface.
• Easier model making thanks to high thixotropy.
• High resistance to fracture when released from the impression.

Technical data:

• Mixing proportions 30 ml / 100 g.
• Mixing time (vacuum) 30 s.
• Mixing time (manual) 60 – 90 s.
• Setting time 10 -14 min.
• Release time from the impression 45 min.
• Compressive resistance (after 1h ) 25 ± 2 MPa [> 20 MPa]
• Linear expansion (after 2 hours ) max. 0.15% [< 0.20 %]

Packaging:

• 5kg.

Gypsum class III. Stodent blue 25 kg

Stodent III is a type 3 hard plaster recommended for antagonist models and working models when making removable and skeletal dentures.

Description:

• Available in blue.
• Small expansion.
• Good mechanical properties.

Advantages:

• Smooth surface.
• Easier model making thanks to high thixotropy.
• High resistance to fracture when released from the impression.

Technical data:

• Mixing proportions 30 ml / 100 g.
• Mixing time (vacuum) 30 s.
• Mixing time (manual) 60 – 90 s.
• Setting time 10 -14 min.
• Release time from the impression 45 min.
• Compressive resistance (after 1h ) 25 ± 2 MPa [> 20 MPa]
• Linear expansion (after 2 hours ) max. 0.15% [< 0.20 %]

Packaging:

• 25kg

Attention:

• Due to the heavy weight of the goods (25 kg), an additional fee will be added to the shipment.

Gypsum class III EcoStone Ortho Natural white 5 kg

Plaster for working models when making removable orthodontic appliances.

Characteristic:

• Low degree of linear expansion.

• Glossy white color.

• High liquidity.

Advantages:

• Smooth surface.

• Easy to prepare and process.

• Surface resistance to abrasion.

Parameters:

• White color.
• Mixing proportions 30 ml / 100 g.
• Setting time 10 - 12 min.
• Linear expansion after 2 hours < 0.13%.

Packaging:

• 5kg

Gypsum class III Stodent blue 3kg

Stodent III is a type 3 hard plaster recommended for antagonist models and working models when making removable and skeletal dentures.

Description:

• Available in color: blue
• Small expansion
• Good mechanical properties

Advantages:

• Smooth surface.
• Easier model making thanks to high thixotropy.
• High resistance to fracture when released from the impression.

Technical data:

• Mixing proportions 30 ml / 100 g.
• Mixing time (vacuum) 30 s.
• Mixing time (manual) 60 – 90 s.
• Setting time 10 -14 min.
• Release time from the impression 45 min.
• Compressive resistance (after 1h ) 25 ± 2 MPa [> 20 MPa]
• Linear expansion (after 2 hours ) max. 0.15% [< 0.20 %]

Packaging:

• 3kg

Gypsum III class Hinrizit E expansion white 5kg

Hinrizit E is a dental plaster with a special formula and high bond expansion. This special plaster is used for the production of models and for casing plastic dentures. Due to its large bond expansion, it evens out the shrinkage of the materials from which dentures are made (e.g. SR Ivocap Injection System, Acetal, Deflex, FJP, Valplast). Hinrizit E can be used for all denture plastics.

Application:

• Technique of producing plastic prostheses.

Features:

• White color.

• Water:gypsum ratio - 25:100

• Mixing time in min. - 5-6.

• Hardening time in min. - 10-12.

• Expansion in the setting process – 0.60.

• Compression resistance after 1 hour. - 30 MPa.

• Dry compression resistance - 60 MPa.

Packaging:

• 5kg.

Gypsum III class. EcoStone yellow 25 kg

Hard, yellow type 3 synthetic plaster of high quality, intended for foundry work in the technique of partial dentures, frame dentures and orthodontic appliances. Meets the requirements of the ISO 6873-3 standard. Certificate of Admission No. IL-5629/MS.

advantages:

• Obtaining models with high durability.
• Minimal, uniform expansion coefficient.
• Consistent level of quality.

Physical properties:

• Hardening time: approx. 10 min.
• Compressive strength after 1 h: over 20 N/mm2.
• Hardness after 24 hours over 80 N/mm2.
• Linear expansion after 2 hours : less than 0.14%.

Mixing proportions and method of application:

• Water 100 g: 30 ml.
• Water: gypsum 0.3 ml/g.
• Operating temperature approx. 23 °C.
• Fast in no more than 10 seconds. pour gypsum into water in the proportions given above and wait 20 seconds. until the water is absorbed by the plaster.
• Mechanical mixing: 30 sec.
• Manual mixing: 60 sec.
• During this time, the plaster reaches the optimal consistency for pouring into model molds using a shaker.
• Shaking time: approx. 6 min
• After this time, stop shaking so as not to disturb the crystallization process.

Storage :

• At least 12 months in a tight, moisture-proof packaging.

Packaging:

• 25kg.

Attention:

• Due to the heavy weight of the goods (25 kg), an additional fee will be added to the shipment.

Gypsum class III EcoStone blue 25 kg

High-quality, blue type 3 hard synthetic gypsum, intended for foundry work in the technique of partial dentures, frame dentures and orthodontic appliances. Meets the requirements of the ISO 6873-3 standard.

Advantages:

• Obtaining models with high durability.
• Minimal, uniform expansion coefficient.
• Consistent level of quality.

Physical properties:

• Hardening time: approx. 10-12 minutes.
• Compressive strength after 1 h: over 20 N/mm2.
• Hardness after 24 hours over 80 N/mm2.
• Linear expansion after 2 hours : less than 0.14%.

Mixing proportions and method of application:

• Gypsum: water 100 g: 30 ml.
• Water: gypsum 0.3 ml/g.
• Operating temperature approx. 23°C.
• Fast in no more than 10 seconds. pour gypsum into water in the proportions given above and wait 20 seconds. until the water is absorbed by the plaster.
• Mechanical mixing: 30 sec.
• Manual mixing: 60 sec.
• During this time, the plaster reaches the optimal consistency for pouring into model molds using a shaker.
• Shaking time: approx. 6 min
• After this time, stop shaking so as not to disturb the crystallization process.

Storage :

• At least 12 months in a tight, moisture-proof packaging.

Packaging:

• 25kg.

Attention:

• Due to the heavy weight of the goods (25 kg), an additional fee will be added to the shipment.

Gypsum class III EcoStone Ortho Natural white 25 kg

Plaster for working models when making removable orthodontic appliances.

Characteristic:

• Low degree of linear expansion.

• Glossy white color.

• High liquidity.

Advantages:

• Smooth surface.

• Easy to prepare and process.

• Surface resistance to abrasion.

Parameters:

• White color
• Mixing proportions 30 ml / 100 g.
• Setting time 10 - 12 min.
• Linear expansion after 2 hours < 0.13%.

Packaging:

• 25kg.

Attention:

• Due to the heavy weight of the goods (25 kg), an additional fee will be added to the shipment.

Gypsum class III Stodent light green - mango scent 25kg

Stodent III is a type 3 hard plaster recommended for antagonist models and working models when making removable and skeletal dentures.

Description:

• Light green color enriched with mango aroma.
• Small expansion.
• Good mechanical properties.

Advantages:

• Smooth surface.
• Easier model making thanks to high thixotropy.
• High resistance to fracture when released from the impression.

Technical data:

• Mixing proportions 30 ml / 100 g.
• Mixing time (vacuum) 30 s.
• Mixing time (manual) 60 – 90 s.
• Setting time 10 -14 min.
• Release time from the impression 45 min.
• Compressive resistance (after 1h ) 25 ± 2 MPa [> 20 MPa]
• Linear expansion (after 2 hours ) max. 0.15% [< 0.20 %]

Packaging:

• 25kg

Attention:

• Due to the heavy weight of the goods (25 kg), an additional fee will be added to the shipment.