PoliDent PMMA X-RAY 98.5 mm
PMMA X-RAY discs enable visibility of tooth positioning in X-ray computed tomography for planning and determining implant treatment.
Thanks to its homogeneous mixture (made of PMMA with barium sulfate), it provides the best visibility in X-ray imaging and prevents light scattering.
Characteristic:
- Vickers hardness: min 26 HV;
- bending strength: min. 114 MPa;
- modulus of elasticity: min. 2771 MPa;
- residual monomer: <1%.
Packaging:
- 1pc.
VOCO CediTEC Denture Base 98x30mm
PMMA for the production of removable denture plates.
Characteristics:
- PMMA with high impact resistance and durability enabling long-term use of the prosthesis;
- high quality denture plates;
- two shades to achieve an aesthetic effect (pink, orange pink);
- very good polishability – can be customized at any time;
- aesthetic, precise, individual – dentures with the CediTEC system.
Indications:
- manufacturing of removable denture plates.
Packaging:
- 1pc.
PoliDent PMMA multilayer disc 98X18mm
PMMA Multilayer discs are recommended for making temporary crowns and bridges and for verifying the bridge on a working model or the oral cavity before the final milling process of the zirconium oxide restoration.
Available in the open 98mm system.
Technical data:
- Extremely easy to process.
- Accurate color matching.
- Bending strength: 114 MPa.
- Vickers hardness: 26 HV.
- E-modulus: 2771 MPa.
- Residual monomer <1%.
Packaging:
- 1 piece
PoliDent PMMA multilayer disc 98X20mm
PMMA Multilayer Premia discs are recommended for making temporary crowns and bridges and for verifying the bridge on a working model or the oral cavity before the final milling process of the zirconium oxide restoration.
Available in the open 98mm system.
Technical data:
- Extremely easy to process.
- Accurate color matching.
- Bending strength: 114 MPa.
- Vickers hardness: 26 HV.
- E-modulus: 2771 MPa.
- Residual monomer <1%.
Packaging:
- 1 piece
PoliDent PMMA multilayer disc 98X16mm
PMMA Multilayer discs are recommended for making temporary crowns and bridges and for verifying the bridge on a working model or the oral cavity before the final milling process of the zirconium oxide restoration. Available in the open 98mm system
Technical data:
- Extremely easy to process
- Accurate color matching
- Bending strength: 114 MPa
- Vickers hardness: 26 HV
- E-modulus: 2771 MPa
- Residual monomer <1%
Packaging:
1 piece
Zirconium PMMA multilayer 98x18mm
Zirconium PMMA Multilayer.
Advantages:
- Multilayer staining guarantees aesthetics similar to natural teeth.
- Dedicated to performing temporary prosthetic works.
- Class IIa medical device.
- Size 98mmx18mm.
Packaging:
- 1 piece
Zirconium PMMA multilayer 98x20mm
Zirconium PMMA Multilayer.
Advantages:
- Multilayer staining guarantees aesthetics similar to natural teeth.
- Dedicated to performing temporary prosthetic works.
- Class IIa medical device.
- Size 98mmx20mm.
Packaging:
- 1 piece
Zirconium PMMA multilayer 98x16mm
Zirconium PMMA Multilayer.
Advantages:
- Multilayer staining guarantees aesthetics similar to natural teeth.
- Dedicated to performing temporary prosthetic works
- Class IIa medical device
- Size 98mmx16mm
Packaging:
- 1 piece
Zirconium PMMA multilayer 98x14mm
Zirconium PMMA Multilayer.
Advantages:
- Multilayer staining guarantees aesthetics similar to natural teeth.
- Dedicated to performing temporary prosthetic works.
- Class IIa medical device.
- Size 98mmx14mm.
Packaging:
- 1 piece