Ips d.Sign 96 High gold-content porcelain alloy Specially developed for metal structures used in conjunction with IPS d.Sign Fluoroapatite Glass Ceramics. It can also be used to make metal structures for IPS Classic and IPS Inline ceramics and others.

Indications:

• Recommended for making inlays / onlays,
• partial crowns,
• total crowns,
• telescopic and conical crowns,
• crown-root inlays,
• bridges with short and long spans.

The percentage composition:

• Au - 73.8
• Fri - 8.5
• Pd - 5.4
• Ag - 9.0
• In - 1.9
• Nb - <1
• Mn - <
• Fe - <1
• Ta - <1
• Li - <1
• Ru - <1
• Re - <1

Technical data:

• Type - 4
• Color - yellow
• Density (g / cmł) - 16.7
• Melting temperature (° C) - 1050 - 1170
• Casting temperature (° C) - 1225 - 1285
• Modulus of elasticity (MPa) - 92.00
• CTE 25 - 500 ° C - 14.3
• CTE 20 - 600 ° C - 14.5
• Elongation (%) - 14.0
• Hardness on the Vickers scale - 215
• Yield point (0.2% elongation) (MPa) - 405

Package:

5g

A noble alloy with a high content of gold and platinum, yellow color (compatible with ceramics available on the market), stiff enough for the construction of short and long bridges.

Application:

• Crowns and bridges.
• Onlay.
• Telescopic beams and crowns.

Composition:

• Au - 78.5%

• Fri - 9.8%

• Pd - 7.7%

• In - 3.7%

Physical properties:

• Yellow color

• Density: 17.6 g / cm

• Melting range: 1110-1230 C

• Pouring temperature: 1400 ° C

• Preheating temperature: 800 ° C

• CET (25-500 C, 25-600 C): 13.9 - 14.1

• Metal-ceramic adhesion (Schwickerat Crack Initiation Test): 34.38 MPa

• Modulus of elasticity: 102 GPa

• Elasticity limit: 510-580 MPa

• Elongation (fracture): 12-8%

• Tensile strength: 630-680

• Vickers hardness HV5 / 30: 220-250-290