Kromotypo 4 super hard plaster 5kg

Extra hard class IV prosthetic plaster with a chromatic setting phase indicator for making models with high compressive and abrasion resistance.

Characteristics:

• final color: pastel yellow;
• water to powder ratio: 22 ml/100 g;
• absorption time: 20 seconds;
• mixing time (manual): 60 seconds;
• mixing time (mechanical): 30 seconds;
• pouring time: 3 minutes;
• setting time: 7 minutes;
• Separation time after setting: 25-30 minutes.
• expansion setting (after 2 hours): 0.08%;
• Compressive strength (after 24 hours): 81 MPa, 11,740 psi, 828 kg/cm²;
• Rockwell hardness (after 24 hours): 85 HRL.

Packaging:

• 5kg

Plaster IV Stodent cream - vanilla scent 3kg

Stodent IV is a super-hard dental plaster type 4 recommended for making working models of fixed skeletal dentures, as well as flexible dentures, combined works, and post-implantation dentures.

Description:

• cream color with a vanilla scent;
• small expansion;
• good liquidity.

Advantages:

• very good detail reproduction;
• smooth surface;
• high resistance to mechanical damage.

Technical data:

• mixing proportions 20 ml / 100 g;
• mixing time (in vacuum) 30 s;
• mixing time (manual) 60 – 90 s;
• setting time 8 -12 min;
• compressive strength (after 1h ) 45 ± 2 MPa [> 35 MPa];
• linear expansion (after 2h ) max. 0.10% [< 0.15 %];
• Linear expansion after 24h < 0.18* %.

Packaging:

• 3kg

Plaster IV class Stodent ash - strawberry scent 3kg

Stodent IV is a super-hard dental plaster type 4 recommended for making working models of fixed skeletal dentures and flexible dentures, combined works, and post-implantation dentures.

Description:

• ash-gray color with a strawberry scent;
• small expansion;
• good liquidity.

Advantages:

• very good detail reproduction;
• smooth surface;
• high resistance to mechanical damage.

Technical data:

• mixing proportions 20 ml / 100 g;
• mixing time (in vacuum) 30 s;
• mixing time (manual) 60 – 90 s;
• setting time 8 -12 min;
• compressive strength (after 1h ) 45 ± 2 MPa [> 35 MPa];
• linear expansion (after 2h ) max. 0.10% [< 0.15 %];
• Linear expansion after 24h < 0.18* %.

Packaging:

• 3kg

Fujirock EP Premium Line Pastel Yellow plaster 11kg

GC Fujirock EP Premium Line Super Hard Plaster, Pastel Yellow.

Advantages:

• for performing high-precision techniques such as work on implants and complex all-ceramic work;
• improved plaster composition and improved color setting;
• scanning capability;
• high fluidity and thixotropic properties.

Physical data:

• pastel yellow;
• powder/liquid ratio 20 ml : 100 g;
• hand mixing - 15 sec;
• vacuum mixing 45 s;
• setting time 9-12 min;
• expansion after setting < 0.09%;
• compressive strength after 1 h approx. 60 N/mm.

Packaging:

• 11kg

Plaster IV class.Stodent brown 6kg

Stodent IV is a super-hard dental plaster type 4 recommended for making working models of fixed skeletal dentures, as well as flexible dentures, combined works, and post-implantation dentures.

Description:

• brown color;
• small expansion;
• good liquidity.

Advantages:

• very good detail reproduction;
• smooth surface;
• high resistance to mechanical damage.

Technical data:

• mixing proportions 20 ml / 100 g;
• mixing time (in vacuum) 30 s;
• mixing time (manual) 60 – 90 s;
• setting time 8 -12 min;
• compressive strength (after 1h ) 45 ± 2 MPa [> 35 MPa];
• linear expansion (after 2h ) max. 0.10% [< 0.15 %];
• Linear expansion after 24h < 0.18* %.

Packaging:

• 6kg

Gypsum class IV EcoStone Base FL for bases dark blue 5 kg

Class IV plaster for model bases, perfectly flowing, dark blue in color.

Advantages:

• very liquid consistency;
• does not require work with a vibrating table;
• no air bubbles between pins;
• low expansion;
• absolutely smooth surface;
• high final hardness;
• big time saver.

Physical properties:

• setting time 10-12 min;
• dry compressive strength 70 Mpa.

Linear expansion:

• after 2 hours 0.06%;

Preparation:

• gypsum / distilled water : 100g / 23 ml;
• operating temperature 23 ° C.

Packaging;

• 5kg

FujiRock IV class EP Classic Golden Brown plaster 12kg

FujiRock IV class EP Classic super-hard plaster type IV, for all prosthetic works requiring the highest precision, strength and stability.

Advantages:

• very resistant to breakage;
• liquid;
• stable around edges;
• long processing time;
• short tie;
• very high plasticity and simultaneous thixotropy;
• excellent handling and bubble-free pouring;
• ability to scan.

Physical data:

• powder/liquid ratio - 20 ml : 100 g;
• hand mixing - 15 seconds;
• vacuum mixing - 45 seconds;
• golden brown color;
• setting time 10-13 minutes;
• expansion after setting after 2 h ≤ 0.09%;
• compressive strength after 1 h approx. 53 MPa.

Packaging:

• 12kg

Fujirock IV class Premium Line Polar White plaster 4kg

GC Fujirock EP Premium Line Polar White for high-precision techniques such as implant work and complex full ceramic work

Advantages:

• improved powder composition and improved color setting;
• ability to scan.

Physical data:

• color polar white;
• setting time 9-12 min;
• expansion after setting < 0.09%;
• compressive strength after 1 h approx. 60 N/mm.

Packaging:

• 4kg

Gypsum class IV EcoStone Natural Premium gold-brown 5 kg

Gypsum class IV Eco Stone Natural Premium super hard plaster recommended for posts and divided models.

Advantages:

• High stability.
• Very smooth surface.
• Scratch resistant.
• It shows high precision.

Technical data :

• Water to plaster ratio: 22/100.
• Setting time: 12-14 min.
• Linear expansion after 2 hours less than 0.09%.
• Gold-brown color.

Packaging:

• 5kg

Plaster IV class Elite Rock sandy brown 3kg

Class IV plaster for working models when making permanent dentures, combined works, post-implantation dentures, etc. Sand color.

Parameters:

• Water / Powder 20 ml / 100 g
• Mixing time (manual) - 1:00 min
• Mixing time (vacuum) - 00:30 sec
• Working time 12 min
• Setting time 14 min
• Release time 45 min
• Expansion after 2 hours 0.08%
• Expansion after 48 hours 0.19%
• Compressive strength 1h 52 MPa (530 kg/cm2)
• Compressive strength 48 h 81 MPa (826 kg/cm2)

Packaging:

• 3kg.

Stodent plaster cream class IV vanilla 1kg

Stodent IV is a super-hard dental plaster type 4 recommended for making working models of fixed skeletal dentures and flexible dentures, combined works, and post-implantation dentures.

Characteristics:

• cream color with a vanilla scent;
• small expansion;
• good liquidity;
• very good detail reproduction;
• smooth surface;
• high resistance to mechanical damage.

Technical data:

• mixing proportions 20 ml / 100 g;
• mixing time (in vacuum) 30 s;
• mixing time (manual) 60 – 90 s;
• setting time 8 -12 min;
• compressive strength (after 1h ) 45 ± 2 MPa [> 35 MPa];
• linear expansion (after 2h ) max. 0.10% [< 0.15 %];
• Linear expansion after 24h < 0.18* %.

Packaging:

• 1kg

Fujirock EP Classic Golden Brown plaster 5 kg

GC Fujirock EP is a class 4 plaster of the highest quality. Designed to perform all prosthetic works, with the highest precision, exceptional hardness and resistance to deformation. Very high plasticity while being thixotropic, excellent handling and pouring without air bubbles. Scanable.

Physical data:

• Golden-brown color.
• Setting time 10-13 min.
• Expansion after setting after 2 h ≤ 0.09%.
• compressive strength after 1 hour approx. 53 MPa.

Packaging:

• 5kg.

Fujirock EP Premium Line Titanium Gray plaster 4 kg

Gypsum class IV For highly precise work on implants and complex all-ceramic work. Improved plaster composition and improved color setting. Scanable.

Physical data:

• Grey colour.
• Setting time 9-12 min.
• Expansion after setting after 2 hours approx. 0.09%.
• Compressive strength after 1 hour approx. 60 N/mm2.

Packaging:

• 4kg

Plaster IV class.Stodent brown 25kg

Stodent IV is a super-hard dental plaster type 4 recommended for making working models of fixed skeletal dentures, as well as flexible dentures, combined works, and post-implantation dentures.

Description:

• brown color;
• small expansion;
• good liquidity.

Advantages:

• very good detail reproduction;
• smooth surface;
• high resistance to mechanical damage.

Technical data:

• mixing proportions 20 ml / 100 g;
• mixing time (in vacuum) 30 s;
• mixing time (manual) 60 – 90 s;
• setting time 8 -12 min;
• compressive strength (after 1h ) 45 ± 2 MPa [> 35 MPa];
• linear expansion (after 2h ) max. 0.10% [< 0.15 %];
• Linear expansion after 24h < 0.18* %.

Packaging:

• 25kg

Attention:

• Due to the heavy weight of the goods (25 kg), an additional fee will be added to the shipment.

Gypsum class IV. Marble Stone Evolution - expansion gypsum in pressure injection processes 3kg

Special double-expansion plaster for duplicating models.

Characteristic:

• White color.
• It does not require the use of a special liquid, mixed with demineralized water.
• Dedicated to work with devices injecting thermoplastic materials.

Packaging:

• 3kg

Gypsum class IV Kimberlite gold 2kg

High-quality modeling plaster, class IV, of natural origin.

Advantages:

• Releases from the impression precisely and easily (only 20 minutes!).
• Thixotropic.
• Very high durability.
• It allows you to obtain excellent results when working with optical scanning systems.

Instructions for use:

• Powder/water ratio: 100 g / 20 ml.
• Operating temperature: 20-23 °C.
• Mechanical mixing in vacuum: 30 seconds.
• Manual mixing: 60 seconds.

Physical properties:

• Working time: 7 min.
• Start of hardening: 9 min.
• End of hardening: 13 min.
• Expansion (2 hours): 0.08%.
• Hardness (24 hours): 247 N/mm2.
• Crushing strength (1g): 58 N/mm2.

Packaging:

• 2Kg

Gypsum class IV, Diamant synthetic gold, 2kg

High-quality synthetic modeling plaster. Perfect for all types of fixed dentures, residual limbs and master models.

Advantages:

• Releases from the impression precisely and easily (only 20 minutes!).
• Thixotropic.
• Very high durability.
• It allows you to obtain excellent results when working with optical scanning systems.

Instructions for use:

• Powder/water ratio: 100 g / 20 ml.
• Operating temperature: 20-23 °C.
• Mechanical mixing in vacuum: 30 seconds.
• Manual mixing: 60 seconds.

Physical properties:

• Working time: 8 min.
• Start of hardening: 10 min.
• End of hardening: 15 minutes.
• Expansion (2 hours): 0.08%.
• Hardness (24 hours): 268 N/mm2.
• Crushing strength (1g): 60 N/mm2.

Packaging:

• 2kg

Gypsum class IV Natural pink rubin 5kg

Class IV plaster for super-hard Rubinite models, pink, natural color. Perfect for working with frames and thermal injection techniques.

Features:

• Mixing proportions: 22-24 ml/ 100 g.
• Working time: 7 min.
• Setting time: 12 min.
• Expansion after setting: 0.10%.
• Compressive strength: 40 MPa.

Packaging:

• 5kg.

Flu-Stone class IV plaster for Indian RED bases 2kg

Class IV plaster for the base, red.

Features:

• Proportions: 24 ml/ 100 gk
• Working time: 6 min.
• Setting time: 11 min
• Expansion after setting: 0.05%
• Compressive strength (1h): 40 Mpa

Packaging:

• 2kg

Plaster IV class EcoStone Base FL for bases, orange, 5 kg

Class IV plaster for model bases, with excellent flow, orange color.

Advantages:

• Very liquid consistency.
• It does not require work with a vibrating table.
• No air bubbles between the pins.
• Low expansion.
• Absolutely smooth surface.
• High final hardness.
• Big time savings.

Physical properties:

• Setting time 10-12 minutes.
• Dry compressive strength 70 MPa.

Linear expansion:

• After 2 hours 0.06%

Preparation:

• Gypsum / distilled water: 100g / 23 ml.
• Operating temperature 23°C.

Packaging:

• 5kg

Gypsum class IV EcoStone Ortho Premium super white 5kg

Class IV Eco Stone Ortho Premium super white gypsum enriched with synthetic material. Very suitable for diagnostic and demonstration models, for orthodontics and under porcelain.

Parameters:

• Manual mixing time - 60 sec.
• Mixing time in a mixer - 30 sec.
• Setting time - 10-12 min.
• Expansion after 2 hours - 0.14%.
• Water to plaster ratio 26-27 ml: 100 g.

Packaging:

• 5kg

Plaster IV class Resin Plaster Plus for implants, gray 2 kg

A combination of high-quality plastic and class IV plaster, super-hard, ideal for prosthetic work on implants.

Description:

• Grey colour.
• Working time 7 min.
• Start of hardening 8 min.
• End of hardening 10 minutes.
• Total hardening time 30 min.
• Expansion (2h): 0.10%.
• Compressive strength (1 h): 50 MP.
• Powder to water ratio 100g/20ml.
• Operating temperature 20-23 degrees ° C.
• Mixing mechanically and in vacuum for 30 seconds.

Packaging:

• 2kg

Gypsum class IV Expander - expansion 3kg

EXPANDER expansion plaster

Characteristics:

• For making working models using acetal-based thermoplastic injection technology.
• Effectively compensates for plastic shrinkage after injection.
• Ensures the best possible fit of thermoplastic dentures to the prosthetic field.

Libra:

• 3kg

Plaster IV class Hinristone Saphir 5 kg Promotion buy 5 pieces pay for 4 pieces

SPECIAL OFFER;

• Buy 5 pieces (you can mix colors) and you will pay for 4 pieces.

Gip IV class.Hinristone Saphir.

Extremely durable, hard plaster with a "snap-set" effect that allows you to remove the post (stump) and work on it after just 30 minutes.

Characteristic:

• creamy, but very flowing consistency;
• high tricsotropic index;
• low expansion;
• excellent CAD/CAM scanning properties;
• homogeneous and delamination-free structure.

Technical data:

• water to plaster ratio 20:100;
• working time 6-7 min;
• setting time 12-14 min;
• binding expansion 0.08% after 2h;
• compressive strength, dry 90 MPa.

Colors:

• golden brown;
• grey;
• ivory;
• pastel yellow.

Packaging:

• 5kg

Plaster IV class.Stodent brown 3kg

Stodent IV is a super-hard dental plaster type 4 recommended for making working models of fixed skeletal dentures, as well as flexible dentures, combined works, and post-implantation dentures.

Description:

• brown color;
• small expansion;
• good liquidity.

Advantages:

• very good detail reproduction;
• smooth surface;
• high resistance to mechanical damage.

Technical data:

• mixing proportions 20 ml / 100 g;
• mixing time (in vacuum) 30 s;
• mixing time (manual) 60 – 90 s;
• setting time 8 -12 min;
• compressive strength (after 1h ) 45 ± 2 MPa [> 35 MPa];
• linear expansion (after 2h ) max. 0.10% [< 0.15 %];
• Linear expansion after 24h < 0.18* %.

Packaging:

• 3kg

Gypsum class IV Resin Gypsum 2 kg, peach color

A combination of high-quality plastic and class IV plaster, super-hard, ideal for prosthetic work on implants. Peach colour.

Technical data:

• Working time 7 min
• Start of hardening 8 min
• End of hardening 10 minutes
• Total hardening time 30 min
• Expansion (2h): 0.10%
• Compressive strength (1 h): 50 MP
• powder to water ratio 100g/20ml
• operating temperature 20-23 degrees C
• mechanical and vacuum mixing for 30 seconds

Packaging:

• 2kg

Fujirock EP Premium Line Pastel Yellow plaster 4 kg

GC Fujirock EP Premium Line Super Hard Plaster, Pastel Yellow - 4kg

Class IV plaster. For high-precision techniques such as implant work and complex all-ceramic work. Improved plaster composition and improved color setting. Scanable.

Physical data:

• Pastel yellow color.
• Setting time 9-12 min.
• Expansion after setting < 0.09%.
• Compressive strength after 1 hour approx. 60 N/mm.

Packaging:

• 4kg

Gypsum IV class Flu-Stone for Terra bases 2 kg Promotion

Grade IV plaster on the base of terra color.

Properties:

• consistency: 24 ml / 100 g
• working time: 6 min.
• setting time: 11 min
• expansion after setting: 0.05%
• compressive strength (1h): 40 Mpa

Package:

2 kg

Gypsum class IV. Base Stone FL white 5kg

Super-hard plaster with excellent fluidity for making model bases without the use of a vibrator. The initial consistency becomes more fluid as the mixing time increases, and flows optimally during pouring.

Application:

• Bases of dental arches in split models.
• All pin systems using plaster.

parameters:

• White color.
• Water-gypsum ratio 23:100.
• Mixing time in minutes 5-6.
• Hardening time in min. 10-12.
• Expansion in the setting process 0.06.
• Compressive strength after 1 hour 50 MPa.
• Dry compressive strength 70 MPa.

Packaging:

• 5 kg.

Plaster IV class EcoStone Natural Premium gold-brown 25 kg

Gypsum class IV Eco Stone Natural Premium super hard plaster recommended for posts and divided models.

Advantages:

• High stability.
• Very smooth surface.
• Scratch resistant.
• It shows high precision.

Technical data :

• Water to plaster ratio: 22/100.
• Setting time: 12-14 min.
• Linear expansion after 2 hours less than 0.09%.
• Gold-brown color.

Packaging:

• 25kg

Attention:

• Due to the heavy weight of the goods (25 kg), an additional fee will be added to the shipment.

Gypsum class IV EcoStone Base FL for dark blue bases, 25 kg

Class IV plaster for model bases, perfectly flowing, dark blue in color.

Advantages:

• Very liquid consistency.
• It does not require work with a vibrating table.
• No air bubbles between the pins.
• Low expansion.
• Absolutely smooth surface.
• High final hardness.
• Big time savings.

Physical properties:

• Setting time 10-12 minutes.
• Dry compressive strength 70 MPa.

Linear expansion:

• After 2 hours 0.06%

Preparation:

• Gypsum / distilled water: 100g / 23 ml.
• Operating temperature 23 °C.

Packaging:

• 25kg

Attention:

• Due to the heavy weight of the goods (25 kg), an additional fee will be added to the shipment.

Gypsum class IV EcoStone Ortho Premium super white 25kg

Class IV Eco Stone Ortho Premium gypsum, super white, enriched with synthetic material. Very suitable for diagnostic and demonstration models, for orthodontics and under porcelain.

Parameters:

• Manual mixing time - 60 sec.
• Mixing time in a mixer - 30 sec.
• Setting time - 10 -12 minutes.
• Expansion after 2 hours - 0.14%.

Packaging:

• 25kg.

Attention:

• Due to the heavy weight of the goods (25 kg), an additional fee will be added to the shipment.

Gypsum class IV Natural pink rubin 25 kg

Class IV plaster for super-hard Rubinite models, pink, natural color. Perfect for working with frames and thermal injection techniques.

Features:

• Mixing proportions: 22-24 ml/ 100 g
• Working time: 7 min.
• Setting time: 12 min
• Expansion after setting: 0.10%
• Compressive strength: 40 MPa

Attention:

• Due to the heavy weight of the goods (25 kg), an additional fee will be added to the shipment.

Packaging:

• 25kg.

Gypsum class IV Kimberlite gold 12 kg

High-quality modeling plaster of natural origin.

Advantages:

• Releases from the impression precisely and easily (only 20 minutes!).
• Thixotropic.
• Very high durability.
• It allows you to obtain excellent results when working with optical scanning systems.

Instructions for use:

• Powder/water ratio: 100 g / 20 ml.
• Operating temperature: 20-23 °C.
• Mechanical mixing in vacuum: 30 seconds. -Hand mixing: 60 seconds.

Physical properties:

• Working time: 7 min.
• Start of hardening: 9 min.
• End of hardening: 13 min.
• Expansion (2 hours): 0.08%.
• Hardness (24 hours): 247 N/mm2.
• Crushing strength (1g): 58 N/mm2.

Packaging:

• 12Kg (6x2kg)

Gypsum IV class Resin Gypsum 12 kg peach

A combination of high-quality plastic and class IV gypsum, super hard, ideal for prosthetic works on implants. Peach colour.

Technical data:

• Working time 7 min.
• Start of hardening 8 min.
• End of hardening 10 min.
• Total hardening time 30 min.
• Expansion (2h): 0.10%.
• Compressive strength (1 h): 50 MP.
• powder to water ratio 100g/20ml.
• working temperature 20-23 degrees °C.
• mechanical mixing and vacuum 30sec.

Packaging:

• 12kg (6x2kg)

Plaster IV class Resin Plaster Plus for implants, gray 12 kg

A combination of high-quality plastic and class IV plaster, super-hard, ideal for prosthetic work on implants.

Technical data:

• Grey colour.
• Working time 7 min.
• Start of hardening 8 min.
• End of hardening 10 minutes.
• Total hardening time 30 min.
• Expansion (2h): 0.10%.
• Compressive strength (1 h): 50 MP.
• powder to water ratio 100g/20ml.
• operating temperature 20-23 degrees °C.
• mechanical and vacuum mixing for 30 seconds.

Packaging:

• 12 kg (6x2kg)

Gypsum class IV, Diamant synthetic gold, 12kg

High-quality synthetic modeling plaster. Perfect for all types of fixed dentures, residual limbs and master models.

Advantages:

• Releases from the impression precisely and easily (only 20 minutes!).
• Thixotropic.
• Very high durability.
• It allows you to obtain excellent results when working with optical scanning systems.

Instructions for use:

• Powder/water ratio: 100 g / 20 ml.
• Operating temperature: 20-23 °C.
• Mechanical mixing in vacuum: 30 seconds.
• Manual mixing: 60 seconds.

Physical properties:

• Working time: 8 min.
• Start of hardening: 10 min.
• End of hardening: 15 minutes.
• Expansion (2 hours): 0.08%.
• Hardness (24 hours): 268 N/mm2.
• Crushing strength (1g): 60 N/mm2.

Packaging:

• 12 kg (6x2kg)

Kromotypo 4 super hard gypsum 25kg

Kromptypo 4. Class IV extra hard prosthetic plaster with chromatic setting phase indicator for making models with high compressive and abrasion resistance.

Characteristics:

• Final color: pastel yellow.
• Water to powder ratio: 22ml/100g.
• Absorption time: 20 seconds.
• Mixing time (manual): 60 seconds.
• Mixing time (mechanical): 30 seconds.
• Pouring time: 3 minutes.
• Setting time: 7 minutes.
• Separation time after setting: 25-30 minutes.
• Expansion setting (after 2 hours): 0.08%
• Compressive strength (after 24 hours): 81 MPa, 11,740 psi, 828 kg/cm2.
• Rockwell hardness (after 24 hours): 85 HRL.

Packaging:

• 25kg

Plaster IV class EcoStone Base FL for bases, orange, 25 kg

Class IV plaster for model bases with excellent flow, orange color.

Advantages:

• Very liquid consistency.
• It does not require work with a vibrating table.
• No air bubbles between the pins.
• Low expansion.
• Absolutely smooth surface.
• High final hardness.
• Big time savings.

Physical properties:

• Setting time 10-12 minutes.
• Dry compressive strength 70 MPa.

Linear expansion:

• After 2 hours 0.06%

Preparation:

• Gypsum / distilled water: 100g / 23 ml.
• Operating temperature 23 °C.

Packaging:

• 25kg

Attention:

• Due to the heavy weight of the goods (25 kg), an additional fee will be added to the shipment.

Plaster IV Stodent cream - vanilla scent 25kg

Stodent IV is a super-hard dental plaster type 4 recommended for making working models of fixed skeletal dentures and flexible dentures, combined works, and post-implantation dentures.

Characteristics:

• cream color with a vanilla scent;
• small expansion;
• good liquidity;
• very good detail reproduction;
• smooth surface;
• high resistance to mechanical damage.

Technical data:

• mixing proportions 20 ml / 100 g;
• mixing time (in vacuum) 30 s;
• mixing time (manual) 60 – 90 s;
• setting time 8 -12 min;
• compressive strength (after 1h ) 45 ± 2 MPa [> 35 MPa];
• linear expansion (after 2h ) max. 0.10% [< 0.15 %];
• Linear expansion after 24h < 0.18* %.

Packaging:

• 25kg

Attention:

• Due to the heavy weight of the goods (25 kg), an additional fee will be added to the shipment.

Plaster IV Stodent ash-gray - strawberry scent 25kg

Stodent IV is a super-hard dental plaster type 4 recommended for making working models of fixed skeletal dentures and flexible dentures, combined works, and post-implantation dentures.

Characteristics:

• ash gray color with a strawberry scent;
• small expansion;
• high liquidity.
• very good detail reproduction;
• smooth surface;
• high resistance to mechanical damage.

Technical data:

• mixing proportions 20 ml / 100 g;
• mixing time (in vacuum) 30 s;
• mixing time (manual) 60 – 90 s;
• setting time 8 -12 min;
• compressive strength (after 1h ) 45 ± 2 MPa [> 35 MPa];
• linear expansion (after 2h ) max. 0.10% [< 0.15 %];
• Linear expansion after 24h < 0.18* %.

Packaging:

• 25kg

Attention:

• Due to the heavy weight of the goods (25 kg), an additional fee will be added to the shipment.