ProBase Cold polymer Pink or Pink V 500g
ProBase Cold is a self-polymerizing acrylic material.
ProBase Cold dentures can be made using two different techniques - pouring and applying.
In both cases, work of the highest quality is obtained.
Characteristics:
- Color Pink or Pink V (pink or pink with veins)
- ease of working with the material;
- constancy of shape and color;
- two work techniques;
- no cadmium in the dye;
- compliance with EN ISO 1567.
Indications:
- complete dentures;
- partial dentures;
- relining of dentures;
- repairs.
Packaging:
- 500g
Triplex Cold polymer PV 500 g
Triplex Cold powder, a cold polymerizing acrylic material.
Characteristics:
- designed for making dentures using the pouring technique and for repairs;
- Polymerization should take place in a pressure apparatus for 15 minutes at a temperature of 40 °C and a pressure of 2-6 bar;
- color PV pink with veins.
Indications:
- partial dentures;
- combined dentures;
- repairs;
- relining.
Packaging:
- 500g
Vertex Castapress monomer 250ml
Vertex Castapress acrylic fluid for cold polymerization.
Packaging:
- 250ml
Vertex Castapress polymer 500g
Vertex Castapres cold polymerizing acrylic.
Characteristics:
- color 4: colorless;
- color 10: transparent pink with veins;
- polymerizes at 55 °C under a pressure of 2.5 bar for 30 minutes;
- easy and convenient to use.
Application:
- complete dentures;
- partial dentures;
- frame prostheses;
- relining of dentures;
- denture repairs;
- Rebasing of full and partial dentures made of cold-curing acrylics.
Packaging:
- 500g
Vertex Castapress polymer 1000g
Vertex Castapress cold polymerizing acrylic.
Characteristics:
- color 10 pink with veins;
- color 4 colorless;
- Vertex Castapress polymerizes at 55 °C under a pressure of 2.5 bar for 30 minutes;
- easy and convenient to use.
Application:
- complete dentures;
- partial dentures;
- frame prostheses;
- denture relines;
- denture repairs;
- rebasing of full and partial dentures made of cold-curing acrylics.
Packaging:
- 1000g
ProBase Cold Clear polymer 500 g
ProBase Cold is a self-polymerizing acrylic material.
ProBase Cold dentures can be made using two different techniques - pouring and applying.
In both cases, work of the highest quality is obtained.
Characteristics:
- color colorless;
- ease of working with the material;
- constancy of shape and color;
- two work techniques;
- no cadmium in the dye;
- compliance with EN ISO 1567.
Indications:
- complete dentures;
- partial dentures;
- denture relining:
- repairs.
Packaging:
- 500g
Futura Press LT polymer 1000g
FuturaPress LT is a cold polymerization acrylic.
Colors:
- colorless;
- pink with veins;
- pink transparent with veins.
Characteristics:
- for making acrylic elements of skeletal prostheses;
- for relining and repairing dentures.
Advantages:
- excellent physical properties;
- high color stability;
- low shrinkage.
Packaging:
- 1000g
Villacryl SP 500g/300ml + Stodent plaster IV class cream vanilla 1kg
Acrylic material intended for the production of acrylic parts in skeletal dentures, as well as for the production of complete dentures using the pouring method.
It can also be used to repair dentures or to create temporary or immediate dentures.
Colors:
- 0 colorless;
- V2 milky pink veined;
- V4 pink veined.
Characteristics:
- easy to prepare and process;
- enables quick production of a prosthesis using the pouring method using silicone pre-pourings;
- ensures the patient's comfort when using the prosthesis;
- well masks the metal structure of the skeletal prosthesis;
- high aesthetics of the prosthesis thanks to its natural color;
- colour stability;
- does not contain heavy metals;
- biologically neutral.
Technical data:
- mixing proportions – acrylic parts of frame dentures: 10 g powder / 7 ml (6.5 g) liquid;
- casting time – acrylic parts of frame dentures: 60-90 s (23 °C);
- polymerization process – acrylic parts of frame dentures: 50-60 °C minimum 20 min. 2 bar;
- fracture strength: > 60* MPa;
- solubility: < 8* µg/mm³;
- sorption: < 32* µg/mm³;
- mixing proportions – infusion-based dentures: 10 g powder / 5.2 ml (5 g) liquid;
- casting time – poured dentures: 30-60 s (23 °C);
- polymerization process – poured dentures: 60 °C 30 min. 2 bar.
Packaging:
- 500g powder/300ml liquid
MERZ Dental Weropress cold acrylic polymer 1000 g
Cold-polymerizing, colour-stable plastic mass based on methyl methacrylate for the preparation of partial and full dentures by injection, extrusion, pressing or casting.
Colors:
- pink transparent with V-10 veins;
- dark pink opaque with veins C34.
Scope of application:
- complete dentures;
- hybrid and overlay dentures;
- finishing and completing combined fixed-removable dentures;
- fixing teeth on cast frames;
- relining;
- repairs, extensions;
- occlusal aids, production of splints.
Packaging:
- 1kg
Futura Press LT Polymer Pink with Strings 500g
FuturaPress LT is a cold polymerization acrylic.
Colors:
- pink with veins.
Characteristics:
- for making acrylic elements of skeletal prostheses;
- for relining and repairing dentures.
Advantages:
- excellent physical properties;
- high color stability;
- low shrinkage.
Packaging:
- 500g
Villacryl S monomer 200ml or 500ml
Villacryl S self-polymerizing fluid for denture repairs.
Packaging:
- 200ml or 500ml
Vertex Castavaria 1000g
Vertex Castavaria pressure-curing acrylic for the production of full and partial dentures using the pouring technique.
Characteristics:
- minimized shrinkage;
- color stability;
- extended liquid phase.
Application:
- complete dentures;
- skeletal prostheses.
Technical data:
- dough phase: 8 <…> 9 minutes;
- working time: 13 minutes;
- curing time: 30 minutes at 55°C and 2.5 bar pressure;
- mixing ratio by volume/parts by weight: 1 ml / 0.95 g liquid (monomer)1.7 g powder (polymer);
- impact resistance: 8.3 kJ/m²;
- bending strength: 79 MPa;
- modulus of elasticity in bending: 2316 MPa;
- water sorption: 23.2 µg/mm³;
- Solubility: 1.8 µg/mm³
Packaging:
- 1000g
FuturaGen for pouring method polymer 1000g
Acrylic for pouring and cold methods, with very low shrinkage - 2%.
Application:
- complete dentures;
- partial dentures;
- repairs and relining.
Characteristics:
- high gloss and exceptionally smooth surface;
- good fit;
- short processing time.
Packaging:
- 1kg
Villacryl SP monomer 300 ml
Liquid for Villacryl SP.
For making acrylic parts in skeletal dentures, as well as for making complete dentures using the pouring method.
It can also be used to repair dentures or to create temporary or immediate dentures.
Packaging:
- 300ml
Vertex Castapress monomer 1000ml
Vertex Castapress acrylic fluid for cold polymerization.
Packaging:
- 1000ml
Vertex Castapress polymer 4000 g
Vertex Castapress cold polymerizing acrylic.
Characteristics:
- color 10 pink with veins;
- color 4 colorless;
- Vertex Castapress polymerizes at 55 °C under a pressure of 2.5 bar for 30 minutes;
- easy and convenient to use.
Application:
- complete dentures;
- partial dentures;
- frame prostheses;
- denture relines;
- denture repairs;
- rebasing of full and partial dentures made of cold-curing acrylics.
Packaging:
- 4000g
Vertex Castavaria color 10 polymer 4000g
Vertex Castavaria pressure-curing acrylic for the production of full and partial dentures using the pouring technique.
Characteristics:
- color 10 pink transparent with veins;
- minimized shrinkage;
- color stability;
- extended liquid phase.
Application:
- complete dentures;
- skeletal prostheses.
Technical data:
- dough phase: 8 <…> 9 minutes;
- working time: 13 minutes;
- curing time: 30 minutes at 55°C and 2.5 bar pressure;
- mixing ratio by volume/parts by weight: 1 ml / 0.95 g liquid (monomer)1.7 g powder (polymer);
- impact resistance: 8.3 kJ/m²;
- bending strength: 79 MPa;
- modulus of elasticity in bending: 2316 MPa;
- water sorption: 23.2 µg/mm³;
- Solubility: 1.8 µg/mm³
Packaging:
- 4000g
Villacryl SP polymer 500g
Acrylic material intended for the production of acrylic parts in skeletal dentures, as well as for the production of complete dentures using the pouring method.
It can also be used to repair dentures or to create temporary or immediate dentures.
Colors;
- 0 colorless;
- V2 milky pink veined;
- V4 pink veined.
Characteristics:
- easy to prepare and process;
- enables quick production of a prosthesis using the pouring method using silicone pre-pourings;
- ensures the patient's comfort when using the prosthesis;
- well masks the metal structure of the skeletal prosthesis;
- high aesthetics of the prosthesis thanks to its natural color;
- colour stability;
- does not contain heavy metals;
- biologically neutral.
Packaging:
- 500g
Vertex Castavaria monomer 1000 ml
Vertex Castavaria acrylic fluid for the pouring technique.
Packaging:
- 1000ml
FuturaGen Com4 polymer color pink 1000g NEW
Cold curing acrylic, perfect for the pouring method.
Application:
- complete dentures;
- partial restorations;
- denture repairs;
- relining of dentures.
Characteristics:
- minimal residual monomer content, which increases safety of use;
- high mechanical strength, making it also suitable for making occlusal splints;
- very good adaptation thanks to reduced polymerization shrinkage, which is especially important when working on implants;
- smooth surface reduces plaque build-up;
- color pink.
Packaging:
- 1kg
Vertex CP 4000g color 10 +2x1000 ml set
Vertex Castapress cold polymerizing acrylic.
Characteristics:
- polymerizes at 55 C under a pressure of 2.5 bar for 30 minutes;
- easy and convenient to use.
Application:
- complete dentures;
- partial dentures;
- frame prostheses;
- denture relines;
- denture repairs;
- rebasing of full and partial dentures made of cold-curing acrylics.
Packaging:
- 4000 g powder color 10 pink transparent with veins
- 2x1000ml liquid
Aplodent Cold polymer 100g
Aplodent Cold is a cold polymerization acrylic material intended for the repair of removable full and partial dentures, acrylic parts of frame dentures and acrylic orthodontic appliances.
Colors:
- 0 – colorless;
- V26 – pink veined;
- V27 – milky pink veined;
- T41 – reddish pink.
Advantages:
- short waiting time to start work;
- fast polymerization only 10 minutes;
- the same color range as in Aplodent Hot, guarantees high aesthetics of the repair;
- contains only organic pigments and is cadmium-free.
Technical data:
- mixing proportions: 10 g powder / 7 ml liquid;
- Dough shelf life: about 10 min. (at 23°C);
- polymerization time: minimum 10 min – 55°C 2 bar;
- fracture strength: > 60* MPa;
- solubility: < 8* µg/mm3;
- sorption: < 32* µg/mm3.
Packaging:
- 100g
Aplodent Cold polymer 500g
Aplodent Cold is a cold polymerization acrylic material intended for the repair of removable full and partial dentures, acrylic parts of frame dentures and acrylic orthodontic appliances.
Colors:
- 0 – colorless;
- V26 – pink veined;
- V27 – milky veined pink;
- T41 – reddish pink.
Advantages:
- short waiting time to start work;
- fast polymerization only 10 minutes;
- the same color range as in Aplodent Hot, guarantees high aesthetics of the repair;
- contains only organic pigments and is cadmium-free.
Technical data:
- mixing proportions: 10 g powder / 7 ml liquid;
- Dough shelf life: about 10 min. (at 23°C);
- polymerization time: minimum 10 min – 55°C 2 bar;
- fracture strength: > 60* MPa;
- solubility: < 8* µg/mm3;
- sorption: < 32* µg/mm3.
Packaging:
- 500g
Aplodent Cold polymer 1000g
Aplodent Cold is a cold polymerization acrylic material intended for the repair of removable full and partial dentures, acrylic parts of frame dentures and acrylic orthodontic appliances.
Colors:
- 0 – colorless;
- V26 – pink veined;
- V27 – milky veined pink;
- T41 – reddish pink.
Advantages:
- short waiting time to start work;
- fast polymerization only 10 minutes;
- the same color range as in Aplodent Hot, guarantees high aesthetics of the repair;
- contains only organic pigments and is cadmium-free.
Technical data:
- mixing proportions: 10 g powder / 7 ml liquid;
- Dough shelf life: about 10 min. (at 23°C);
- polymerization time: minimum 10 min – 55°C 2 bar;
- fracture strength: > 60* MPa;
- solubility: < 8* µg/mm3;
- sorption: < 32* µg/mm3.
Packaging:
- 1000g
Aplodent Cold polymer 2kg
Aplodent Cold is a cold polymerization acrylic material intended for the repair of removable full and partial dentures, acrylic parts of frame dentures and acrylic orthodontic appliances.
Colors:
- 0 – colorless;
- V26 – pink veined;
- V27 – milky pink veined;
- T41 – reddish pink.
Advantages:
- short waiting time to start work;
- fast polymerization only 10 minutes;
- the same color range as in Aplodent Hot, guarantees high aesthetics of the repair;
- contains only organic pigments and is cadmium-free.
Technical data:
- mixing proportions: 10 g powder / 7 ml liquid;
- Dough shelf life: about 10 min. (at 23°C);
- polymerization time: minimum 10 min – 55°C 2 bar;
- fracture strength: > 60* MPa;
- solubility: < 8* µg/mm3;
- sorption: < 32* µg/mm3.
Packaging:
- 2000g
Aplodent Cold polymer 4kg
Aplodent Cold is a cold polymerization acrylic material intended for the repair of removable full and partial dentures, acrylic parts of frame dentures and acrylic orthodontic appliances.
Colors:
- 0 – colorless;
- V26 – pink veined;
- V27 – milky pink veined;
- T41 – reddish pink.
Advantages:
- short waiting time to start work;
- fast polymerization only 10 minutes;
- the same color range as in Aplodent Hot, guarantees high aesthetics of the repair;
- contains only organic pigments and is cadmium-free.
Technical data:
- mixing proportions: 10 g powder / 7 ml liquid;
- Dough shelf life: about 10 min. (at 23°C);
- polymerization time: minimum 10 min – 55°C 2 bar;
- fracture strength: > 60* MPa;
- solubility: < 8* µg/mm3;
- sorption: < 32* µg/mm3.
Packaging:
- 4000g
Villacryl SP V4 500g/300ml set 4+1 Free
Acrylic material intended for the production of acrylic parts in skeletal dentures, as well as for the production of complete dentures using the pouring method.
It can also be used to repair dentures or to create temporary or immediate dentures.
Characteristics:
- easy to prepare and process;
- enables quick production of a prosthesis using the pouring method using silicone pre-pourings;
- ensures the patient's comfort when using the prosthesis;
- well masks the metal structure of the skeletal prosthesis;
- high aesthetics of the prosthesis thanks to its natural color;
- colour stability;
- does not contain heavy metals;
- biologically neutral.
Packaging:
- 5x 500g powder/300ml liquid