Zirconium Explore Esthetic 98x12mm

Zirconium Explore Esthetic, new generation zircon, up to 5 layers of multilayer translucency. Thanks to increased strength in the gingival area and increased translucency in the enamel area, it allows for a very wide range of applications while maintaining high aesthetics of the restoration.

Parameters:

• Strength after sintering 727 MPa - 1000 MPa.
• Translucency 47%- 48.8%
• Sintering temperature 1480 °C

Application:

• Foundations.
• Crowns.
• 3-point bridges.
• Bridge with a suspension (not recommended for patients with bruxism).

Zirconium is a new line of materials based on zirconium oxide intended for use in CAD/CAM technology.

Zirconium products are certified by SFDA, ISO13485, CE and FDA.

Thanks to a two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconium discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconium discs.

Packaging:

• 1 piece

Zirconium Explore Hybrid 98x30mm + Gingiva 20ml

Discover tooth restoration with UPCERA Explore Hybrid.

Explore Hybrid disc with a diameter of 30 mm, designed to smoothly adapt to the natural structure of the teeth. Say goodbye to the limitations of typical gradient discs with Explore Hybrid. Effortlessly achieve light to dark pink gums. A solid base ensures durability and transparency. Thanks to Explore Hybrid, you will never lose the color of your gums again.

Sintering parameters:

• 1150°C 4°C/min 30 min
• 1300°C 2°C/min -1480°C 4°C/min 150min
• 800°C -8°C/min
• Open at 500°C

Packaging:

• 1 pc + Gingiva 20ml

Zirconium HT White 98x10mm

Zirconium is a new line of materials based on zirconium oxide designed for use in cad/cam technology. Zirconium products are SFDA, ISO13485, CE and FDA certified. Thanks to the two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconium discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconia discs.

HT - High translucent

Characteristics:

• Recommended for foundations.
• Very high strength.

Destiny:

• Cap.
• Bridges.
• 3-4 point bridge.
• Bridge with overhang ((not recommended for patients with bruxism).
• Inlay bridge (not recommended for patients with bruxism).
• Maryland bridge (not recommended for patients with bruxism).
• Telescopic crown.
• Individual connectors.

Chemical composition:

• ZrO2 + HfO2 + Y2O3 - >99%
• Y2O3 - 4.5%~6%
• HfO2 - <5%
• Al2O3 - <0.5%
• Other oxides - <0.5%

Physical properties:

• Density before sintering - 3.1+0.5g/cm3

• Density after sintering - 6.08+0.01g/cm3

• CTE (25- 500°C) 10.05+1.0×10- 6K- 1

• Strength after sintering - 1300 Mpa

• Percentage of monoclinic accelerated aging (%) - <15%

• Average transparency - 39%

• Cytotoxicity test - 0

• Radioactivity - <0.1Bq/g

• Sintering temperature - 1530°C

Packaging:

• 1 piece

Outlet Zirconium AG Explore Functional B1 89-71-16 short expiry date

Zirconium AG Explore Functional color B1 89-71-16 short expiry date.

Packaging:

• 1 piece

Outlet Zirconium AG ST Color D2 89-71-20mm short expiry date

Zirconium AG ST Color D2 89-71-20mm short expiry date.

Packaging:

• 1 piece

Outlet Zirconium AG ST Color D2 89-71-25mm short expiry date

Zirconium AG ST Color D2 89-71-25mm short expiry date.

Packaging:

• 1 piece

Outlet Zirconium ZZ Explore Functional B1 95x14mm

Zirconium ZZ Explore Functional color B1 95x14mm

Packaging:

• 1 piece

Zirconium HT White 38x12mm

Zirconium is a new line of materials based on zirconium oxide designed for use in cad/cam technology. Zirconium products are SFDA, ISO13485, CE and FDA certified. Thanks to the two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconium discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconia discs.

HT - High translucent

Characteristics:

• Recommended for foundations.
• Very high strength.

Destiny:

• Cap
• Bridges
• 3-4 point bridge
• Suspended bridge (not recommended for patients with bruxism).
• Inlay bridge (not recommended for patients with bruxism).
• Maryland bridge (not recommended for patients with bruxism).
• Telescopic crown.
• Individual connectors.

Chemical composition:

• ZrO2 + HfO2 + Y2O3 - >99%
• Y2O3 - 4.5%~6%
• HfO2 - <5%
• Al2O3 - <0.5%
• Other oxides - <0.5%

Physical properties:

• Density before sintering - 3.1+0.5g/cm3

• Density after sintering - 6.08+0.01g/cm3

• CTE (25- 500°C) 10.05+1.0×10- 6K- 1

• Strength after sintering - 1300 Mpa

• Percentage of monoclinic accelerated aging (%) - <15%

• Average transparency - 39%

• Cytotoxicity test - 0

• Radioactivity - <0.1Bq/g

• Sintering temperature - 1530°C

Packaging:

• 1 piece

Zirconium HT White 98x14mm

Zirconium is a new line of materials based on zirconium oxide designed for use in cad/cam technology. Zirconium products are SFDA, ISO13485, CE and FDA certified. Thanks to the two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconium discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconia discs.

HT - High translucent

Characteristics:

• Recommended for foundations.
• Very high strength.

Destiny:

• Cap.
• Bridges.
• 3-4 point bridge.
• Suspended bridge (not recommended for patients with bruxism).
• Inlay bridge (not recommended for patients with bruxism).
• Maryland bridge (not recommended for patients with bruxism).
• Telescopic crown.
• Individual connectors.

Chemical composition:

• ZrO2 + HfO2 + Y2O3 - >99%
• Y2O3 - 4.5%~6%
• HfO2 - <5%
• Al2O3 - <0.5%
• Other oxides - <0.5%

Physical properties:

• Density before sintering - 3.1+0.5g/cm3

• Density after sintering - 6.08+0.01g/cm3

• CTE (25- 500°C) 10.05+1.0×10- 6K- 1

• Strength after sintering - 1300 Mpa

• Percentage of monoclinic phase accelerated aging (%) - <15%

• Average transparency - 43%

• Cytotoxicity test - 0

• Radioactivity - <0.1Bq/g

• Sintering temperature - 1530°C

Packaging:

• 1 piece

Zirconium HT White 98x16mm

Zirconium is a new line of materials based on zirconium oxide designed for use in cad/cam technology. Zirconium products are SFDA, ISO13485, CE and FDA certified. Thanks to the two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconium discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconia discs.

HT - High translucent

Characteristics:

• Recommended for foundations.
• Very high strength.

Destiny:

• Cap
• Bridges
• 3-4 point bridge
• Suspended bridge (not recommended for patients with bruxism).
• Inlay bridge (not recommended for patients with bruxism).
• Maryland bridge (not recommended for patients with bruxism).
• Telescopic crown.
• Individual connectors.

Chemical composition:

• ZrO2 + HfO2 + Y2O3 - >99%
• Y2O3 - 4.5%~6%
• HfO2 - <5%
• Al2O3 - <0.5%
• Other oxides - <0.5%

Physical properties:

• Density before sintering - 3.1+0.5g/cm3

• Density after sintering - 6.08+0.01g/cm3

• CTE (25- 500°C) 10.05+1.0×10- 6K- 1

• Strength after sintering - 1300 Mpa

• Percentage of monoclinic accelerated aging (%) - <15%

• Average transparency - 39%

• Cytotoxicity test - 0

• Radioactivity - <0.1Bq/g

• Sintering temperature - 1530°C

Packaging:

• 1 piece

Zirconium ST Color 98x10mm

Zirconium is a new line of materials based on zirconium oxide designed for use in cad/cam technology. Zirconium products are SFDA, ISO13485, CE and FDA certified. Thanks to the two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconium discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconia discs.

ST-Super translucent

Characteristics:

• Recommended for works in full anatomical shape in the posterior section.

Destiny:

• Cap.
• Bridges.
• 3-4 point bridge.
• Suspended bridge (not recommended for patients with bruxism).
• Inlay bridge (not recommended for patients with bruxism).
• Maryland bridge (not recommended for patients with bruxism).
• Telescopic crown.
• Individual connectors.

Chemical composition:

• ZrO2 + HfO2 + Y2O3 >98%
• Fe2O3 <0.3%
• Pr2O3 <0.3%
• Er2O3 <0.3%
• Other oxides <0.5%.

Physical properties:

• Density before sintering - 3.1+0.5g/cm3
• Density after sintering - 6.08+0.01g/cm3
• CTE (25- 500°C) - 10.05+1.0×10- 6K- 1
• Strength after sintering - 1300 MPa
• Percentage of monoclinic aging phase (%) <15%
• Cytotoxicity Test - 0 Level
• Radioactivity <0.1Bq/g
• Sintering temperature 1530°C
• Translucency 43%

Packaging:

• 1 piece

Zirconium ST Color 98x12mm

Zirconium is a new line of materials based on zirconium oxide designed for use in cad/cam technology. Zirconium products are SFDA, ISO13485, CE and FDA certified. Thanks to the two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconium discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconia discs.

ST-Super translucent

Characteristics:

• Recommended for works in full anatomical shape in the posterior section.

Destiny:

• Cap.
• Bridges.
• 3-4 point bridge.
• Suspended bridge (not recommended for patients with bruxism).
• Inlay bridge (not recommended for patients with bruxism).
• Maryland bridge (not recommended for patients with bruxism).
• Telescopic crown.
• Individual connectors.

Chemical composition:

• ZrO2 + HfO2 + Y2O3 >98%
• Fe2O3 <0.3%
• Pr2O3 <0.3%
• Er2O3 <0.3%
• Other oxides <0.5%.

Physical properties:

• Density before sintering - 3.1+0.5g/cm3
• Density after sintering - 6.08+0.01g/cm3
• CTE (25- 500°C) - 10.05+1.0×10- 6K- 1
• Strength after sintering - 1300 MPa
• Percentage of monoclinic aging phase (%) <15%
• Cytotoxicity Test - 0 Level
• Radioactivity <0.1Bq/g
• Sintering temperature 1530°C
• Translucency 43%

Packaging:

• 1 piece

Zirconium ST Color 98x14mm

Zirconium is a new line of materials based on zirconium oxide designed for use in cad/cam technology. Zirconium products are SFDA, ISO13485, CE and FDA certified. Thanks to the two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconium discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconia discs.

ST-Super translucent

Characteristics:

• Recommended for works in full anatomical shape in the posterior section.

Destiny:

• Cap.
• Bridges.
• 3-4 point bridge.
• Suspended bridge (not recommended for patients with bruxism).
• Inlay bridge (not recommended for patients with bruxism).
• Maryland bridge (not recommended for patients with bruxism).
• Telescopic crown.
• Individual connectors.

Chemical composition:

• ZrO2 + HfO2 + Y2O3 >98%
• Fe2O3 <0.3%
• Pr2O3 <0.3%
• Er2O3 <0.3%
• Other oxides <0.5%.

Physical properties:

• Density before sintering - 3.1+0.5g/cm3
• Density after sintering - 6.08+0.01g/cm3
• CTE (25- 500°C) - 10.05+1.0×10- 6K- 1
• Strength after sintering - 1300 MPa
• Percentage of monoclinic aging phase (%) <15%
• Cytotoxicity Test - 0 Level
• Radioactivity <0.1Bq/g
• Sintering temperature 1530°C
• Translucency 43%

Packaging:

• 1 piece

Zirconium HT White 98x18mm

Zirconium is a new line of materials based on zirconium oxide designed for use in cad/cam technology. Zirconium products are SFDA, ISO13485, CE and FDA certified. Thanks to the two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconium discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconia discs.

HT - High translucent

Characteristics:

• Recommended for foundations.
• Very high strength.

Destiny:

• Cap
• Bridges
• 3-4 point bridge
• Suspended bridge (not recommended for patients with bruxism).
• Inlay bridge (not recommended for patients with bruxism).
• Maryland bridge (not recommended for patients with bruxism).
• Telescopic crown.
• Individual connectors.

Chemical composition:

• ZrO2 + HfO2 + Y2O3 - >99%
• Y2O3 - 4.5%~6%
• HfO2 - <5%
• Al2O3 - <0.5%
• Other oxides - <0.5%

Physical properties:

• Density before sintering - 3.1+0.5g/cm3

• Density after sintering - 6.08+0.01g/cm3

• CTE (25- 500°C) 10.05+1.0×10- 6K- 1

• Strength after sintering - 1300 Mpa

• Percentage of monoclinic accelerated aging (%) - <15%

• Average transparency - 39%

• Cytotoxicity test - 0

• Radioactivity - <0.1Bq/g

• Sintering temperature - 1530°C

Packaging:

• 1 piece

Zirconium ST Color 98x16mm

Zirconium is a new line of materials based on zirconium oxide designed for use in cad/cam technology. Zirconium products are SFDA, ISO13485, CE and FDA certified. Thanks to the two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconium discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconia discs.

ST-Super translucent

Characteristics:

• Recommended for works in full anatomical shape in the posterior section.

Destiny:

• Cap.
• Bridges.
• 3-4 point bridge.
• Suspended bridge (not recommended for patients with bruxism).
• Inlay bridge (not recommended for patients with bruxism).
• Maryland bridge (not recommended for patients with bruxism).
• Telescopic crown.
• Individual connectors.

Chemical composition:

• ZrO2 + HfO2 + Y2O3 >98%
• Fe2O3 <0.3%
• Pr2O3 <0.3%
• Er2O3 <0.3%
• Other oxides <0.5%.

Physical properties:

• Density before sintering - 3.1+0.5g/cm3
• Density after sintering - 6.08+0.01g/cm3
• CTE (25- 500°C) - 10.05+1.0×10- 6K- 1
• Strength after sintering - 1300 MPa
• Percentage of monoclinic aging phase (%) <15%
• Cytotoxicity Test - 0 Level
• Radioactivity <0.1Bq/g
• Sintering temperature 1530°C
• Translucency 43%

Packaging:

• 1 piece

Zirconium HT White 98x20mm

Zirconium is a new line of materials based on zirconium oxide designed for use in cad/cam technology. Zirconium products are SFDA, ISO13485, CE and FDA certified. Thanks to the two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconium discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconia discs.

HT - High translucent

Characteristics:

• Recommended for foundations.
• Very high strength.

Destiny:

• Cap
• Bridges
• 3-4 point bridge
• Suspended bridge (not recommended for patients with bruxism).
• Inlay bridge (not recommended for patients with bruxism).
• Maryland bridge (not recommended for patients with bruxism).
• Telescopic crown.
• Individual connectors.

Chemical composition:

• ZrO2 + HfO2 + Y2O3 - >99%
• Y2O3 - 4.5%~6%
• HfO2 - <5%
• Al2O3 - <0.5%
• Other oxides - <0.5%

Physical properties:

• Density before sintering - 3.1+0.5g/cm3

• Density after sintering - 6.08+0.01g/cm3

• CTE (25- 500°C) 10.05+1.0×10- 6K- 1

• Strength after sintering - 1300 Mpa

• Percentage of monoclinic accelerated aging (%) - <15%

• Average transparency - 39%

• Cytotoxicity test - 0

• Radioactivity - <0.1Bq/g

• Sintering temperature - 1530°C

Packaging:

• 1 piece

Zirconium HT ZZ 95x14mm

Zirconium is a new line of materials based on zirconium oxide designed for use in cad/cam technology. Zirconium products are SFDA, ISO13485, CE and FDA certified. Thanks to the two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconium discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconia discs.

HT - High translucent

Characteristics:

• Recommended for foundations.
• Very high strength.

Destiny:

• Cap
• Bridges
• 3-4 point bridge
• Suspended bridge (not recommended for patients with bruxism).
• Inlay bridge (not recommended for patients with bruxism).
• Maryland bridge (not recommended for patients with bruxism).
• Telescopic crown.
• Individual connectors.

Chemical composition:

• ZrO2 + HfO2 + Y2O3 - >99%
• Y2O3 - 4.5%~6%
• HfO2 - <5%
• Al2O3 - <0.5%
• Other oxides - <0.5%

Physical properties:

• Density before sintering - 3.1+0.5g/cm3

• Density after sintering - 6.08+0.01g/cm3

• CTE (25- 500°C) 10.05+1.0×10- 6K- 1

• Strength after sintering - 1300 Mpa

• Percentage of monoclinic accelerated aging (%) - <15%

• Average transparency - 39%

• Cytotoxicity test - 0

• Radioactivity - <0.1Bq/g

• Sintering temperature - 1530°C

Packaging:

• 1 piece

Zirconium AG ST Color 89x71x16mm

Zirconium is a new line of materials based on zirconia designed for use in cad/cam technology. Zirconium products are SFDA, ISO13485, CE and FDA certified. Thanks to the two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconia discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconia discs.

ST-Super translucent

Characteristics:

• Recommended for works in full anatomical shape in the posterior section.

Destiny:

• Cap.
• Bridges.
• 3-4 point bridge.
• Suspended bridge (not recommended for patients with bruxism).
• Inlay bridge (not recommended for patients with bruxism).
• Maryland bridge (not recommended for patients with bruxism).
• Telescopic crown.
• Individual connectors.

Chemical composition:

• ZrO2 + HfO2 + Y2O3 >98%
• Fe2O3 <0.3%
• Pr2O3 <0.3%
• Er2O3 <0.3%
• Other oxides <0.5%.

Physical properties:

• Density before sintering - 3.1+0.5g/cm3
• Density after sintering - 6.08+0.01g/cm3
• CTE (25- 500°C) - 10.05+1.0×10- 6K- 1
• Strength after sintering - 1300 Mpa
• Percentage of monoclinic aging phase (%) <15%
• Cytotoxicity Test - 0 Level
• Radioactivity <0.1Bq/g
• Sintering temperature 1530°C
• Translucency 43%

Packaging:

• 1 piece

Zirconium AG ST Color 89x71x14mm

Zirconium is a new line of materials based on zirconia designed for use in cad/cam technology. Zirconium products are SFDA, ISO13485, CE and FDA certified. Thanks to the two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconia discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconia discs.

ST-Super translucent

Characteristics:

• Recommended for works in full anatomical shape in the posterior section.

Destiny:

• Cap.
• Bridges.
• 3-4 point bridge.
• Suspended bridge (not recommended for patients with bruxism).
• Inlay bridge (not recommended for patients with bruxism).
• Maryland bridge (not recommended for patients with bruxism).
• Telescopic crown.
• Individual connectors.

Chemical composition:

• ZrO2 + HfO2 + Y2O3 >98%
• Fe2O3 <0.3%
• Pr2O3 <0.3%
• Er2O3 <0.3%
• Other oxides <0.5%.

Physical properties:

• Density before sintering - 3.1+0.5g/cm3
• Density after sintering - 6.08+0.01g/cm3
• CTE (25- 500°C) - 10.05+1.0×10- 6K- 1
• Strength after sintering - 1300 Mpa
• Percentage of monoclinic aging phase (%) <15%
• Cytotoxicity Test - 0 Level
• Radioactivity <0.1Bq/g
• Sintering temperature 1530°C
• Translucency 43%

Packaging:

• 1 piece

Zirconium AG ST Color 89x71x12mm

Zirconium is a new line of materials based on zirconia designed for use in cad/cam technology. Zirconium products are SFDA, ISO13485, CE and FDA certified. Thanks to the two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconia discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconia discs.

ST-Super translucent

Characteristics:

• Recommended for works in full anatomical shape in the posterior section.

Destiny:

• Cap.
• Bridges.
• 3-4 point bridge.
• Suspended bridge (not recommended for patients with bruxism).
• Inlay bridge (not recommended for patients with bruxism).
• Maryland bridge (not recommended for patients with bruxism).
• Telescopic crown.
• Individual connectors.

Chemical composition:

• ZrO2 + HfO2 + Y2O3 >98%
• Fe2O3 <0.3%
• Pr2O3 <0.3%
• Er2O3 <0.3%
• Other oxides <0.5%.

Physical properties:

• Density before sintering - 3.1+0.5g/cm3
• Density after sintering - 6.08+0.01g/cm3
• CTE (25- 500°C) - 10.05+1.0×10- 6K- 1
• Strength after sintering - 1300 Mpa
• Percentage of monoclinic aging phase (%) <15%
• Cytotoxicity Test - 0 Level
• Radioactivity <0.1Bq/g
• Sintering temperature 1530°C
• Translucency 43%

Packaging:

• 1 piece

Zirconium AG ST Color 89x71x18mm

Zirconium is a new line of materials based on zirconia designed for use in cad/cam technology. Zirconium products are SFDA, ISO13485, CE and FDA certified. Thanks to the two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconia discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconia discs.

ST-Super translucent

Characteristics:

• Recommended for works in full anatomical shape in the posterior section.

Destiny:

• Cap.
• Bridges.
• 3-4 point bridge.
• Suspended bridge (not recommended for patients with bruxism).
• Inlay bridge (not recommended for patients with bruxism).
• Maryland bridge (not recommended for patients with bruxism).
• Telescopic crown.
• Individual connectors.

Chemical composition:

• ZrO2 + HfO2 + Y2O3 >98%
• Fe2O3 <0.3%
• Pr2O3 <0.3%
• Er2O3 <0.3%
• Other oxides <0.5%.

Physical properties:

• Density before sintering - 3.1+0.5g/cm3
• Density after sintering - 6.08+0.01g/cm3
• CTE (25- 500°C) - 10.05+1.0×10- 6K- 1
• Strength after sintering - 1300 Mpa
• Percentage of monoclinic aging phase (%) <15%
• Cytotoxicity Test - 0 Level
• Radioactivity <0.1Bq/g
• Sintering temperature 1530°C
• Translucency 43%

Packaging:

• 1 piece

Zirconium AG ST Color 89x71x20mm

Zirconium is a new line of materials based on zirconia designed for use in cad/cam technology. Zirconium products are SFDA, ISO13485, CE and FDA certified. Thanks to the two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconia discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconia discs.

ST-Super translucent

Characteristics:

• Recommended for works in full anatomical shape in the posterior section.

Destiny:

• Cap.
• Bridges.
• 3-4 point bridge.
• Suspended bridge (not recommended for patients with bruxism).
• Inlay bridge (not recommended for patients with bruxism).
• Maryland bridge (not recommended for patients with bruxism).
• Telescopic crown.
• Individual connectors.

Chemical composition:

• ZrO2 + HfO2 + Y2O3 >98%
• Fe2O3 <0.3%
• Pr2O3 <0.3%
• Er2O3 <0.3%
• Other oxides <0.5%.

Physical properties:

• Density before sintering - 3.1+0.5g/cm3
• Density after sintering - 6.08+0.01g/cm3
• CTE (25- 500°C) - 10.05+1.0×10- 6K- 1
• Strength after sintering - 1300 Mpa
• Percentage of monoclinic aging phase (%) <15%
• Cytotoxicity Test - 0 Level
• Radioactivity <0.1Bq/g
• Sintering temperature 1530°C
• Translucency 43%

Packaging:

• 1 piece

Zirconium HT White 98x25mm

Zirconium is a new line of materials based on zirconium oxide designed for use in cad/cam technology. Zirconium products are SFDA, ISO13485, CE and FDA certified. Thanks to the two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconium discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconia discs.

HT - High translucent

Characteristics:

• Recommended for foundations.
• Very high strength.

Destiny:

• Cap
• Bridges
• 3-4 point bridge
• Suspended bridge (not recommended for patients with bruxism).
• Inlay bridge (not recommended for patients with bruxism).
• Maryland bridge (not recommended for patients with bruxism).
• Telescopic crown.
• Individual connectors.

Chemical composition:

• ZrO2 + HfO2 + Y2O3 - >99%
• Y2O3 - 4.5%~6%
• HfO2 - <5%
• Al2O3 - <0.5%
• Other oxides - <0.5%

Physical properties:

• Density before sintering - 3.1+0.5g/cm3

• Density after sintering - 6.08+0.01g/cm3

• CTE (25- 500°C) 10.05+1.0×10- 6K- 1

• Strength after sintering - 1300 Mpa

• Percentage of monoclinic accelerated aging (%) - <15%

• Average transparency - 39%

• Cytotoxicity test - 0

• Radioactivity - <0.1Bq/g

• Sintering temperature - 1530°C

Packaging:

• 1 piece

Zirconium ST Color 98x18 mm

Zirconium is a new line of zirconium oxide materials designed for use in cad / cam technology. Zirconium products have SFDA, ISO13485, CE and FDA certificates. Due to the two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconium discs are characterized by a homogeneous structure, which is an element characteristic of high-quality zirconium discs.

ST-Super translucent

Characteristics:

• recommended for fully anatomical work in the posterior region

Destiny:

• Cap
• Bridges
• 3- 4 point bridge
• Bridge with an evidence (not recommended for patients with bruxism)
• Bridge on inlays (not recommended for patients with bruxism)
• Maryland bridge (not recommended for patients with bruxism)
• Telescopic crown
• Individual connectors

Chemical composition:

• ZrO2 + HfO2 + Y2O3> 98%
• Fe2O3 <0.3%
• Pr2O3 <0.3%
• Er2O3 <0.3%
• Other oxides <0.5%.

Physical properties:

• Density before sintering - 3.1 + 0.5g / cm3
• Density after sintering - 6.08 + 0.01 g / cm3
• CTE (25- 500 ° C) - 10.05 + 1.0 × 10- 6K- 1
• Strength after sintering - 1100 Mpa
• Percentage of monoclinic phase aging (%) <15%
• Cytotoxicity testing - 0 Level
• Radioactivity <0.1Bq / g
• Sintering temperature 1530 ° C

Package:

1 piece.

Outlet Zirconium AG ST Multilayered B1 89-71-14mm short expiry date

Zirconium AG ST Multilayered B1 89-71-14mm short shelf life.

Packaging:

• 1 piece

Zirconium HT ZZ 95x16mm

Zirconium is a new line of materials based on zirconia designed for use in cad/cam technology. Zirconium products are SFDA, ISO13485, CE and FDA certified. Thanks to the two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconium discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconia discs.

• HT - High translucent

Characteristics:

• Recommended for foundations.
• Very high strength.

Destiny:

• Cap.
• Bridges.
• 3-4 point bridge.
• Suspended bridge (not recommended for patients with bruxism).
• Inlay bridge (not recommended for patients with bruxism).
• Maryland bridge (not recommended for patients with bruxism).
• Telescopic crown.
• Individual connectors.

Chemical composition:

• ZrO2 + HfO2 + Y2O3 - >99%
• Y2O3 - 4.5%~6%
• HfO2 - <5%
• Al2O3 - <0.5%
• Other oxides - <0.5%

Physical properties:

• Density before sintering - 3.1+0.5g/cm3

• Density after sintering - 6.08+0.01g/cm3

• CTE (25- 500°C) 10.05+1.0×10- 6K- 1

• Strength after sintering - 1300 Mpa

• Percentage of monoclinic accelerated aging (%) - <15%

• Average transparency - 39%

• Cytotoxicity test - 0

• Radioactivity - <0.1Bq/g

• Sintering temperature - 1530°C

Packaging:

• 1 piece

Zirconium HT ZZ 95x12mm

Zirconium is a new line of materials based on zirconium oxide designed for use in cad/cam technology. Zirconium products are SFDA, ISO13485, CE and FDA certified. Thanks to the two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconium discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconia discs.

HT - High translucent

Characteristics:

• Recommended for foundations.
• Very high strength.

Destiny:

• Cap
• Bridges
• 3-4 point bridge
• Suspended bridge (not recommended for patients with bruxism).
• Inlay bridge (not recommended for patients with bruxism).
• Maryland bridge (not recommended for patients with bruxism).
• Telescopic crown.
• Individual connectors.

Chemical composition:

• ZrO2 + HfO2 + Y2O3 - >99%
• Y2O3 - 4.5%~6%
• HfO2 - <5%
• Al2O3 - <0.5%
• Other oxides - <0.5%

Physical properties:

• Density before sintering - 3.1+0.5g/cm3

• Density after sintering - 6.08+0.01g/cm3

• CTE (25- 500°C) 10.05+1.0×10- 6K- 1

• Strength after sintering - 1300 Mpa

• Percentage of monoclinic accelerated aging (%) - <15%

• Average transparency - 39%

• Cytotoxicity test - 0

• Radioactivity - <0.1Bq/g

• Sintering temperature - 1530°C

Packaging:

• 1 piece

Zirconium HT ZZ 95x18mm

Zirconium is a new line of materials based on zirconium oxide designed for use in cad/cam technology. Zirconium products are SFDA, ISO13485, CE and FDA certified. Thanks to the two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconium discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconia discs.

HT - High translucent

Characteristics:

• Recommended for foundations.
• Very high strength.

Destiny:

• Cap
• Bridges
• 3-4 point bridge
• Suspended bridge (not recommended for patients with bruxism).
• Inlay bridge (not recommended for patients with bruxism).
• Maryland bridge (not recommended for patients with bruxism).
• Telescopic crown.
• Individual connectors.

Chemical composition:

• ZrO2 + HfO2 + Y2O3 - >99%
• Y2O3 - 4.5%~6%
• HfO2 - <5%
• Al2O3 - <0.5%
• Other oxides - <0.5%

Physical properties:

• Density before sintering - 3.1+0.5g/cm3

• Density after sintering - 6.08+0.01g/cm3

• CTE (25- 500°C) 10.05+1.0×10- 6K- 1

• Strength after sintering - 1300 Mpa

• Percentage of monoclinic accelerated aging (%) - <15%

• Average transparency - 39%

• Cytotoxicity test - 0

• Radioactivity - <0.1Bq/g

• Sintering temperature - 1530°C

Packaging:

• 1 piece

Zirconium AG HT 89-71-14mm

Zirconium is a new line of materials based on zirconium oxide designed for use in cad/cam technology. Zirconium products are SFDA, ISO13485, CE and FDA certified. Thanks to the two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconium discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconia discs.

HT - High translucent

Characteristics:

• Recommended for foundations.
• Very high strength.

Destiny:

• Cap
• Bridges
• 3-4 point bridge
• Suspended bridge (not recommended for patients with bruxism).
• Inlay bridge (not recommended for patients with bruxism).
• Maryland bridge (not recommended for patients with bruxism).
• Telescopic crown.
• Individual connectors.

Chemical composition:

• ZrO2 + HfO2 + Y2O3 - >99%
• Y2O3 - 4.5%~6%
• HfO2 - <5%
• Al2O3 - <0.5%
• Other oxides - <0.5%

Physical properties:

• Density before sintering - 3.1+0.5g/cm3

• Density after sintering - 6.08+0.01g/cm3

• CTE (25- 500°C) 10.05+1.0×10- 6K- 1

• Strength after sintering - 1300 Mpa

• Percentage of monoclinic accelerated aging (%) - <15%

• Average transparency - 39%

• Cytotoxicity test - 0

• Radioactivity - <0.1Bq/g

• Sintering temperature - 1530°C

Packaging:

• 1 piece

Zirconium ZZ ST Color 95x14mm

Zirconium is a new line of materials based on zirconium oxide designed for use in cad/cam technology. Zirconium products are SFDA, ISO13485, CE and FDA certified. Thanks to the two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconium discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconia discs.

• ST-Super translucent

Characteristics:

• Recommended for works in full anatomical shape in the posterior section.

Destiny:

• Cap.
• Bridges.
• 3-4 point bridge.
• Suspended bridge (not recommended for patients with bruxism).
• Inlay bridge (not recommended for patients with bruxism).
• Maryland bridge (not recommended for patients with bruxism).
• Telescopic crown.
• Individual connectors.

Chemical composition:

• ZrO2 + HfO2 + Y2O3 >98%
• Fe2O3 <0.3%
• Pr2O3 <0.3%
• Er2O3 <0.3%
• Other oxides <0.5%.

Physical properties:

• Density before sintering - 3.1+0.5g/cm3
• Density after sintering - 6.08+0.01g/cm3
• CTE (25- 500°C) - 10.05+1.0×10- 6K- 1
• Strength after sintering - 1300 MPa
• Percentage of monoclinic aging phase (%) <15%
• Cytotoxicity Test - 0 Level
• Radioactivity <0.1Bq/g
• Sintering temperature 1530°C
• Translucency 43%

Packaging:

• 1 piece

Zirconium AG ST 89-71-14mm

Zirconium is a new line of materials based on zirconium oxide designed for use in cad/cam technology. Zirconium products are SFDA, ISO13485, CE and FDA certified. Thanks to the two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconium discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconia discs.

ST-Super translucent

Characteristics:

• Recommended for works in full anatomical shape in the posterior section.

Destiny:

• Cap.
• Bridges.
• 3-4 point bridge.
• Suspended bridge (not recommended for patients with bruxism).
• Inlay bridge (not recommended for patients with bruxism).
• Maryland bridge (not recommended for patients with bruxism).
• Telescopic crown.
• Individual connectors.

Chemical composition:

• ZrO2 + HfO2 + Y2O3 - >99%
• Y2O3 - 4.5%~6%
• HfO2 - <5%
• Al2O3 - <0.5%
• Other oxides - <0.5%

Physical properties:

• Density before sintering - 3.1+0.5g/cm3

• Density after sintering - 6.08+0.01g/cm3

• CTE (25- 500°C) 10.05+1.0×10- 6K- 1

• Strength after sintering - 1300 Mpa

• Percentage of monoclinic phase accelerated aging (%) - <15%

• Average transparency - 43%

• Cytotoxicity test - 0

• Radioactivity - <0.1Bq/g

• Sintering temperature - 1530°C

Packaging:

• 1 piece

Zirconium Explore Functional 98x16mm

Zirconium Explore Functional, new generation zirconium, up to 5 layers of Multilayer translucency. Thanks to increased strength in the gingival area and increased translucency in the enamel area, it allows for a very wide range of applications while maintaining high aesthetics of the restoration.

Parameters:

• Strength after sintering 1027MPa - 1300MPa
• Translucency 43%- 46.6%
• Sintering temperature 1480 °C

Application:

• Foundations.
• Crowns.
• 3-point bridges.
• Multi-point bridges.
• Bridge with a suspension (not recommended for patients with bruxism).

Zirconium is a new line of materials based on zirconium oxide intended for use in CAD/CAM technology. Zirconium products are certified by SFDA, ISO13485, CE and FDA. Thanks to a two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconium discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconium discs.

Packaging:

• 1 piece

Zirconium Explore Functional 98x18mm

Zirconium Explore Functional, new generation zircon, up to 5 layers of Multilayer translucency. Thanks to increased strength in the gingival area and increased translucency in the enamel area, it allows for a very wide range of applications while maintaining high aesthetics of the restoration.

Parameters:

• Strength after sintering 1027MPa - 1300MPa.
• Translucency 43%- 46%
• Sintering temperature 1480 °C

Application:

• Foundations.
• Crowns.
• 3-point bridges.
• Multi-point bridges.
• Bridge with a suspension (not recommended for patients with bruxism).

Zirconium is a new line of materials based on zirconium oxide intended for use in CAD/CAM technology. Zirconium products are certified by SFDA, ISO13485, CE and FDA. Thanks to a two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconium discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconium discs.

Packaging:

• 1 piece

Zirconium Explore Esthetic 98x16mm

Zirconium Explore Esthetic new generation zircon, up to 5 layers of multilayer translucency. Thanks to the increased strength in the gingival area and increased translucency in the enamel area, it allows for a very wide range of applications, while maintaining high aesthetics of the restoration.

parameters:

• Strength after sintering 727MPa- 1000MPa
• Translucency 47% - 48.8%
• Sintering temperature 1480 °C

Application:

• foundations.
• Crowns.
• 3-point bridges.
• Overhang bridge (not recommended for patients with bruxism)

Zirconium is a new line of materials based on zirconium oxide designed for use in cad/cam technology. Zirconium products are SFDA, ISO13485, CE and FDA certified. Thanks to the two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconium discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconia discs.

Packaging:

• 1 piece

Zirconium Explore Esthetic 98x18mm

Zirconium Explore Esthetic new generation zircon, up to 5 layers of multilayer translucency. Thanks to the increased strength in the gingival area and increased translucency in the enamel area, it allows for a very wide range of applications, while maintaining high aesthetics of the restoration.

parameters:

• Strength after sintering 727MPa - 1000MPa
• Translucency 47% - 48.8%
• Sintering temperature 1480 °C

Application:

• foundations.
• crowns.
• 3-point bridges.
• Overhang bridge (not recommended for patients with bruxism)

Zirconium is a new line of materials based on zirconium oxide designed for use in cad/cam technology. Zirconium products are SFDA, ISO13485, CE and FDA certified. Thanks to the two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconia discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconia discs.

Packaging:

• 1 piece

Zirconium AG Explore Esthetic 89-71-18mm

Zirconium Explore Esthetic new generation zircon, up to 5 layers of multilayer translucency. Thanks to the increased strength in the gingival area and increased translucency in the enamel area, it allows for a very wide range of applications, while maintaining high aesthetics of the restoration.

parameters:

• Strength after sintering 727MPa - 1000MPa
• Translucency 47% - 48.8%
• Sintering temperature 1480°C

Application:

• foundations.
• Crowns.
• 3-point bridges.
• Overhang bridge (not recommended for patients with bruxism)

Zirconium is a new line of materials based on zirconium oxide designed for use in cad/cam technology. Zirconium products are SFDA, ISO13485, CE and FDA certified. Thanks to the two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconium discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconia discs.

Packaging:

• 1 piece

Zirconium AG Explore Functional 89-71-18mm

Zirconium Explore Functional new generation zircon, up to 5 layers of multilayer translucency. Thanks to the increased strength in the gingival area and increased translucency in the enamel area, it allows for a very wide range of applications, while maintaining high aesthetics of the restoration.

parameters:

• Strength after sintering 1027MPa - 1300MPa.
• Translucency 43% - 46.6%
• Sintering temperature 1480 °C

Application:

• foundations.
• crowns.
• 3-point bridges.
• Bridge with overhang (not recommended for patients with bruxism).

Zirconium is a new line of materials based on zirconium oxide designed for use in cad/cam technology. Zirconium products are SFDA, ISO13485, CE and FDA certified. Thanks to the two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconium discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconia discs.

Packaging:

• 1 piece

Zirconium Explore Functional 98x20mm

Zirconium Explore Functional new generation zircon, up to 5 layers of multilayer translucency. Thanks to the increased strength in the gingival area and increased translucency in the enamel area, it allows for a very wide range of applications, while maintaining high aesthetics of the restoration.

parameters:

• Strength after sintering 1027MPa - 1300MPa.
• Translucency 43% - 46.6%
• Sintering temperature 1480 °C

Application:

• foundations.
• crowns.
• 3-point bridges.
• Multi-point bridges.
• Bridge with overhang (not recommended for patients with bruxism).

Zirconium is a new line of materials based on zirconium oxide designed for use in cad/cam technology. Zirconium products are SFDA, ISO13485, CE and FDA certified. Thanks to the two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconium discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconia discs.

Packaging:

• 1 piece

Zirconium ZZ ST Color 95x16mm

Zirconium is a new line of materials based on zirconium oxide designed for use in cad/cam technology. Zirconium products are SFDA, ISO13485, CE and FDA certified. Thanks to the two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconium discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconia discs.

ST-Super translucent

Characteristics:

• Recommended for works in full anatomical shape in the posterior section.

Destiny:

• Cap.
• Bridges.
• 3-4 point bridge.
• Suspended bridge (not recommended for patients with bruxism).
• Inlay bridge (not recommended for patients with bruxism).
• Maryland bridge (not recommended for patients with bruxism).
• Telescopic crown.
• Individual connectors.

Chemical composition:

• ZrO2 + HfO2 + Y2O3 >98%
• Fe2O3 <0.3%
• Pr2O3 <0.3%
• Er2O3 <0.3%
• Other oxides <0.5%.

Physical properties:

• Density before sintering - 3.1+0.5g/cm3
• Density after sintering - 6.08+0.01g/cm3
• CTE (25- 500°C) - 10.05+1.0×10- 6K- 1
• Strength after sintering - 1300 MPa
• Percentage of monoclinic aging phase (%) <15%
• Cytotoxicity Test - 0 Level
• Radioactivity <0.1Bq/g
• Sintering temperature 1530°C
• Translucency 43%

Packaging:

• 1 piece

Outlet Zirconium ZZ Explore Esthetic B1 95x14mm short expiry date

Zirconium ZZ Explore Esthetic color B1 95x14mm short shelf life.

Packaging:

• 1 piece

Zirconium AG Explore Functional B1 89-71-16mm

Zirconium Explore Functional, new generation zircon, up to 5 layers of Multilayer translucency. Thanks to increased strength in the gingival area and increased translucency in the enamel area, it allows for a very wide range of applications while maintaining high aesthetics of the restoration.

Parameters:

• Strength after sintering 1027MPa - 1300MPa.
• Translucency 43%- 46.6%
• Sintering temperature 1480 °C

Application:

• Foundations.
• Crowns.
• 3-point bridges.
• Bridge with a suspension (not recommended for patients with bruxism).

Zirconium is a new line of materials based on zirconium oxide intended for use in CAD/CAM technology. Zirconium products are certified by SFDA, ISO13485, CE and FDA. Thanks to a two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconium discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconium discs.

Packaging:

• 1 piece

Outlet Zirconium AG ST Color C3 89-71-20mm short expiry date

Zirconium AG ST Color color C3 89-71-20mm short expiry date.

Packaging:

• 1 piece

Zirconium ZZ Explore Functional 95x14 mm

Zirconium Explore Functional new generation zircon, up to 5 layers of multilayer translucency. Thanks to the increased strength in the gingival area and increased translucency in the enamel area, it allows for a very wide range of applications, while maintaining high aesthetics of the restoration.

parameters:

• Strength after sintering 1027MPa - 1300MPa.
• Translucency 43% - 46.6%
• Sintering temperature 1480 °C.

Application:

• foundations.
• Crowns.
• 3-point bridges.
• Multi-point bridges.
• Bridge with overhang (not recommended for patients with bruxism).

Zirconium is a new line of materials based on zirconium oxide designed for use in cad/cam technology. Zirconium products are SFDA, ISO13485, CE and FDA certified. Thanks to the two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconium discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconia discs.

Packaging:

• 1 piece

Zirconium ZZ Explore Esthetic 95x14mm

Zirconium Explore Esthetic new generation zircon, up to 5 layers of multilayer translucency. Thanks to the increased strength in the gingival area and increased translucency in the enamel area, it allows for a very wide range of applications, while maintaining high aesthetics of the restoration.

parameters:

• Strength after sintering 727MPa - 1000MPa
• Translucency 47% - 48.8%
• Sintering temperature 1480 °C

Application:

• foundations.
• Crowns.
• 3-point bridges.
• Overhang bridge (not recommended for patients with bruxism)

Zirconium is a new line of materials based on zirconium oxide designed for use in cad/cam technology. Zirconium products are SFDA, ISO13485, CE and FDA certified. Thanks to the two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconium discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconia discs.

Packaging:

• 1 piece

Zirconium ZZ TT One Multilayered 95x18mm

Zirconium is a new line of materials based on zirconium oxide designed for use in cad/cam technology. Zirconium products are SFDA, ISO13485, CE and FDA certified. Thanks to the two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconium discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconia discs.

ST-Super translucent

Characteristics:

• Recommended for works in full anatomical shape in the posterior section.

Destiny:

• Cap.
• Bridges.
• 3-4 point bridge.
• Suspended bridge (not recommended for patients with bruxism).
• Inlay bridge (not recommended for patients with bruxism).
• Maryland bridge (not recommended for patients with bruxism).
• Telescopic crown.
• Individual connectors.

Chemical composition:

• ZrO2 + HfO2 + Y2O3 >98%
• Fe2O3 <0.3%
• Pr2O3 <0.3%
• Er2O3 <0.3%
• Other oxides <0.5%.

Physical properties:

• Density before sintering - 3.1+0.5g/cm3
• Density after sintering - 6.08+0.01g/cm3
• CTE (25- 500°C) - 10.05+1.0×10- 6K- 1
• Strength after sintering - 1300 MPa
• Percentage of monoclinic aging phase (%) <15%
• Cytotoxicity Test - 0 Level
• Radioactivity <0.1Bq/g
• Sintering temperature 1530°C
• Translucency 43%

Packaging:

• 1 piece

Zirconium ZZ Explore Functional 95x18mm

Zirconium Explore Functional new generation zircon, up to 5 layers of multilayer translucency. Thanks to the increased strength in the gingival area and increased translucency in the enamel area, it allows for a very wide range of applications, while maintaining high aesthetics of the restoration.

parameters:

• Strength after sintering 1027MPa - 1300MPa.
• Translucency 43% - 46.6%
• Sintering temperature 1480 °C.

Application:

• foundations.
• crowns.
• 3-point bridges.
• Multi-point bridges.
• Bridge with overhang (not recommended for patients with bruxism).

Zirconium is a new line of materials based on zirconia designed for use in cad/cam technology. Zirconium products are SFDA, ISO13485, CE and FDA certified. Thanks to the two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconium discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconia discs.

Packaging:

• 1 piece.

Zirconium ZZ Explore Esthetic 95x18mm

Zirconium Explore Esthetic new generation zircon, up to 5 layers of multilayer translucency. Thanks to the increased strength in the gingival area and increased translucency in the enamel area, it allows for a very wide range of applications, while maintaining high aesthetics of the restoration.

parameters:

• Strength after sintering 727MPa - 1000MPa
• Translucency 47% - 48.8%
• Sintering temperature 1480 °C

Application:

• foundations.
• Crowns.
• 3-point bridges.
• Bridge with overhang (not recommended for patients with bruxism).

Zirconium is a new line of materials based on zirconium oxide designed for use in cad/cam technology. Zirconium products are SFDA, ISO13485, CE and FDA certified. Thanks to the two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconium discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconia discs.

Packaging:

• 1 piece

Zirconium Explore Esthetic 98x14mm

Zirconium Explore Esthetic new generation zircon, up to 5 layers of multilayer translucency. Thanks to the increased strength in the gingival area and increased translucency in the enamel area, it allows for a very wide range of applications, while maintaining high aesthetics of the restoration.

parameters:

• Strength after sintering 727MPa - 1000MPa
• Translucency 47% - 48.8%
• Sintering temperature 1480 °C

Application:

• foundations.
• Crowns.
• 3-point bridges.
• Bridge with overhang (not recommended for patients with bruxism).

Zirconium is a new line of materials based on zirconia designed for use in cad/cam technology. Zirconium products are SFDA, ISO13485, CE and FDA certified. Thanks to the two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconium discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconia discs.

Packaging:

• 1 piece

Zirconium ZZ Explore Esthetic 95x20mm

Zirconium Explore Esthetic new generation zircon, up to 5 layers of multilayer translucency. Thanks to the increased strength in the gingival area and increased translucency in the enamel area, it allows for a very wide range of applications, while maintaining high aesthetics of the restoration.

parameters:

• Strength after sintering 727MPa - 1000MPa
• Translucency 47% - 48.8%
• Sintering temperature 1480 °C

Application:

• foundations.
• crowns.
• 3-point bridges.
• bridge with overhang (not recommended for patients with bruxism).

Zirconium is a new line of materials based on zirconium oxide designed for use in cad/cam technology. Zirconium products are SFDA, ISO13485, CE and FDA certified. Thanks to the two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconium discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconia discs.

Packaging:

• 1 piece

Zirconium ZZ Explore Esthetic 95x16mm

Zirconium Explore Esthetic new generation zircon, up to 5 layers of multilayer translucency. Thanks to the increased strength in the gingival area and increased translucency in the enamel area, it allows for a very wide range of applications, while maintaining high aesthetics of the restoration.

parameters:

• Strength after sintering 727MPa - 1000MPa
• Translucency 47% - 48.8%
• Sintering temperature 1480 °C

Application:

• foundations.
• Crowns.
• 3-point bridges.
• Overhang bridge (not recommended for patients with bruxism)

Zirconium is a new line of materials based on zirconium oxide designed for use in cad/cam technology. Zirconium products are SFDA, ISO13485, CE and FDA certified. Thanks to the two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconium discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconia discs.

Packaging:

• 1 piece