Chrome-cobalt solder (Cobalt-Chrome-Lot)
Soldering rods for all chrome-cobalt alloys for skeleton prostheses.
Characteristics:
- melting temperature range 1100- 1150 °C;
- operating temperature 1180 °C;
- flux - Fluxol;
- percentage composition by weight: Cr 61; Cr 28.5; Mo 3.5; Si 4; Fe;B;C.
Packaging:
- min 4g
Minoxyd soldering flux 80g
Minoxyd flux for soldering precious metal alloys, as well as precious metals with chrome-cobalt or chrome-nickel alloys.
This flux saves time required for indirect soldering and ensures strong and durable joints.
Packaging:
- 80g
Solder for porcelain (Wiron-Lot)
Solder sticks for all chrome-nickel alloys.
Characteristics:
- melting temperature range 1020- 1150 °C;
- operating temperature 1165 °C;
- Fluxol flux;
- percentage composition by weight: Ni 66; Cr 19; Mo 5.5; Fe 5; Si 3.5; B.
Packaging:
- About 4g
Universal low-melting solder 700 °C
Universal low-melting solder.
Characteristics:
- solder in rods with flux;
- universal solder does not contain cadmium on the basis of Ag and Cu;
- operating temperature 700 °C;
- weight 1.2g;
- rod diameter 1.0mm - 1.1mm.
Packaging:
- 1pc
Dentaflux flux 50g
Universal flux for all standard alloys, especially for joints between noble and non-noble alloys.
- Color white.
Packaging:
- 1 pc.
Universal solder in a disc 700 °C 10g
Universal solder in a coil, without flux.
Characteristics:
- operating temperature 700 °C;
- weight 10g;
- without flux;
- not permitted for intraoral use;
- ø 0.60 mm.
Composition:
- Ag - 59.0%;
- Zn - 25.0%;
- Cu - 16.0%.
Packaging:
- 1pc.
Leone orthodontic solder 1x0.5mm disc 10g
Leone R0223-00 orthodontic solder.
Characteristics:
- without flux;
- silver content: 55%;
- melting point: 630° - 660°C.
Packaging:
- 1 pc./10g