Castorit Super C protective mass 150g 1 pc.
Precision investment material for NiCr and CoCr alloys in crown and bridge techniques, containing phosphate for high-shrinkage alloys.
Dentaurum catalog number 106-721-00
Characteristics:
- does not contain carbon and graphite;
- very good consistency of the mixture;
- smooth castings;
- exact fit;
- controlled expansion;
- easy release of castings from casting rings;
- thermal stability;
- application time 4 min.
Physical data:
- working time: 4 min - 5 min;
- preheating: constant preheating, preheating with holding time;
- preheating temperature: 950 °C;
- type: 1;
- class: 1;
- standard: DIN EN ISO 15912;
- color: white;
- compression resistance: 3 MPa - 4 MPa.
Packaging:
- 150g
Castorit Super C 1000ml - The liquid is sensitive to low temperatures - shipping in winter is at the risk of the customer
Castorit super C investment liquid.
Dentaurum catalog number 106-704-00
Attention:
The fluid is sensitive to frost!
Shipping of goods in winter is at the customer's risk.
Packaging:
- 1000ml
Bellavest T shielding mass 160g 1 pc.
Graphite-free investment material for precision casting of crowns and bridges made of precious and non-precious metals.
Characteristics:
- high edge strength and ease of release;
- mixing time at 20 °C - approx. 5 minutes;
- mixing time at 27 °C - approx. 3 minutes;
- total expansion in the ring with 100% BegoSol solution - 3%;
- recommended fluid: BegoSol He and BegoSol.
Packaging:
- 160g
Deguvest liquid 1350ml
Deguvest Impact mass liquid for the traditional mold heating process.
Attention:
- The fluid is sensitive to frost.
- Shipping of goods in winter is at the customer's risk.
Packaging:
- 1350 ml.
Deguvest Impact shielding mass 150g
Deguvest Impact - Universal investment material for crown and bridge techniques.
Characteristics:
- designed for work on all types of dental alloys;
- possibility of using a quick or traditional mold heating process;
- high precision and surface quality of the cast object;
- easy release of the casting;
- without gypsum and carbon content.
Technical data:
- mixing proportions 100 g: 23 ml (powder: liquid);
- total expansion 1.2 – 2.4% (linear);
- mixing time 60 s (in vacuum);
- processing time 4 – 6 min at 23°C;
- compressive strength 4 – 8 N/mm² (depending on the fluid concentration).
Packaging:
- 1 pc./150g
Deguvest Specjal liquid 1350ml - Promotion
Deguvest Special liquid.
Deguvest Impact mass liquid for a quick mold heating process.
Attention:
The fluid is sensitive to frost.
Shipping of goods in winter is at the customer's risk.
Packaging:
- 1350 ml.
Gilvest Liquid for investment mass 1000ml - The liquid is sensitive to low temperatures - shipping in winter at the risk of the customer.
Gilvest liquid for Gilvest MG, MG Speed, Gilvest HS and Gilvest ME.
Attention:
- The fluid is sensitive to frost.
Packaging:
- 1000ml.
Gilvest HS 160g
Fast-setting investment material for crowns and bridges.
Use with GILVEST LIQUID.
Mixing proportions:
- Powder: Liquid 100 g: 25 (24 – 26) ml
How to use:
- provide the required amount of fluid;
- pour in powder;
- mix thoroughly for 30 seconds
- mix for 1 minute in a vacuum mixer at approximately 300 rpm.
Packaging:
- 160g
BegoSol HE 1l - The liquid is sensitive to low temperatures - shipping in winter is at the risk of the ordering party.
BegoSol HE liquid for mixing Bellavest SH and Belavest T investment masses.
Attention:
- The liquid is sensitive to frost - shipping in winter is at the customer's risk.
Packaging:
- 1l.
Bellavest SH shielding mass 160g
Belavest SH is a quick or traditionally heated investment material for precision casting of crowns and bridges.
Also for pressed ceramics, precious and non-precious metals.
Bellavest® SH precision crown and bridge material offers exceptional versatility and flexibility.
Easy to use thanks to the special BegoSol® HE mixing fluid ensuring maximum flexibility in combination with only one fluid.
Characteristics:
- very smooth casting surfaces;
- does not contain graphite, bound with phosphorus;
- hardens with considerable edge strength, can be easily released.
Packaging:
- 1pc/160g
SheraFina 2000 investment for crowns and bridges 160g
SHERAFINA 2000 Refractory mass for crowns and bridges.
Characteristics:
- excellent quality;
- for pressed ceramics;
- for alloys of precious and base metals;
- easy expansion control;
- for quick and slow heating;
- very fine-grained and compact consistency;
- smooth surface of castings;
- very high casting accuracy.
Packaging:
- 1 pc.
SheraFina Rapid investment for crowns and bridges 160g
SHERAFINA-RAPID Investment material for crowns and bridges.
Characteristics:
- for alloys of precious and base metals;
- easy expansion control;
- for quick and slow heating;
- very fine-grained and compact consistency;
- smooth surface of castings;
- very high casting accuracy.
Packaging:
- 1 pc.
Shera Liquid investment material 1l ** The liquid is sensitive to low temperatures - shipping in winter is at the customer's risk**
SHERALIQUID
Liquid for all SHERA investment materials.
Packaging:
- 1l
Castorit Super C 40x150g weight + 1 l Liquid
Precision investment material for NiCr and CoCr alloys in crown and bridge techniques, containing phosphate for high-shrinkage alloys.
Characteristics:
- does not contain carbon and graphite;
- very good consistency of the mixture;
- smooth castings;
- exact fit;
- controlled expansion;
- easy release of castings from casting rings;
- thermal stability;
- application time 4 min.
Physical data:
- working time: 4 min - 5 min;
- preheating: constant preheating, preheating with holding time;
- preheating temperature: 950 °C;
- type: 1;
- class: 1;
- standard: DIN EN ISO 15912;
- color: white;
- compressive strength: 3 MPa - 4 MPa.
Packaging:
- 40 pcs. x 150g + 1l liquid
Gilvest HS carton 40x160g + Free Liquid
Fast-setting investment material for crowns and bridges.
Use with GILVEST LIQUID.
Mixing proportions:
- Powder : Liquid 100 g : 25 (24 – 26) ml
How to use:
- provide the required amount of fluid;
- pour in the powder;
- mix thoroughly for 30 seconds;
- mix for 1 minute in a vacuum mixer at approximately 300 rpm.
Packaging:
- 160g x 40 pcs + liquid 1l
Bellavest SH cardboard covering mass 80x160g
Belavest SH is a quick or traditionally heated investment material for precision casting of crowns and bridges.
Also for pressed ceramics, precious and non-precious metals.
Bellavest® SH precision crown and bridge material offers exceptional versatility and flexibility.
Easy to use thanks to the special BegoSol® HE mixing fluid ensuring maximum flexibility in combination with only one fluid.
Characteristics:
- very smooth casting surfaces;
- does not contain graphite, bound with phosphorus;
- hardens with considerable edge strength, can be easily released.
Packaging:
- 80x160g
Deguvest Impact 50x150g - cardboard
Deguvest Impact - Universal investment material for crown and bridge techniques.
Characteristics:
- designed for work on all types of dental alloys;
- possibility of using a quick or traditional mold heating process;
- high precision and surface quality of the cast object;
- easy release of the casting;
- without gypsum and carbon content.
Technical data:
- mixing proportions 100 g: 23 ml (powder: liquid);
- total expansion 1.2 – 2.4% (linear);
- mixing time 60 s (in vacuum);
- processing time 4 – 6 min at 23°C;
- compressive strength 4 – 8 N/mm² (depending on the fluid concentration).
Packaging:
- 50pcs.x150g
Castorit Super C carton 40x150g
Precision investment material for NiCr and CoCr alloys in crown and bridge techniques, containing phosphate for high-shrinkage alloys.
Characteristics:
- does not contain carbon and graphite;
- very good consistency of the mixture;
- smooth castings;
- exact fit;
- controlled expansion;
- easy release of castings from casting rings;
- thermal stability;
- application time 4 min.
Physical data:
- working time: 4 min - 5 min;
- preheating: constant preheating, preheating with holding time;
- preheating temperature: 950 °C;
- type: 1;
- class: 1;
- standard: DIN EN ISO 15912;
- color: white;
- compression resistance: 3 MPa - 4 MPa.
Packaging:
- 40 pcs x 150g
Bellavest DR shielding mass 160g
BEGO Bellavest DR - a new, precise, dust-reduced Shock-heat investment material for crowns and bridges.
Characteristics:
- dust formation during work reduced by approximately 80% has a positive impact on health protection;
- Shock heating up to 900°C or conventional heating means flexibility in a modern dental laboratory;
- very good flow parameters and extended operating time of up to 5 minutes improve the user's comfort;
- creamy consistency leads to very smooth surfaces of cast objects with perfect reproduction of the smallest details;
- constant high quality and optimal expansion control lead to high precision and accuracy in all indications;
- after setting, it offers high edge strength and leads to correct casting of the smallest details;
- The good technical parameters of the mass emphasize its universal character and lead to savings in time and material.
Fine dust reduction:
- Bellavest DR is an excellent crown and bridge material designed for those dental technicians who place great emphasis on health protection in their laboratory;
- Unlike conventional phosphate masses, approximately 80% less harmful quartz-containing dust is produced during the preparation of Bellavest DR mass.
Rapid or conventional heating:
- Bellavest DR is designed for technicians who use both conventional and rapid burn-in methods;
- it also does not matter whether the work is made of precious or base metal alloys.
Easy processing and high safety:
- Bellavest DR mass is exceptionally fine-grained and has excellent flow parameters;
- despite its high marginal strength, it allows for easy release of cast objects;
- the mass is prepared together with BegoSol HE liquid in a mixer using vacuum;
- at an ambient temperature of 20°C, the technician has about 5 minutes to freely fill several rings with mass in one cycle;
- very smooth and exceptionally precise.
Packaging:
- 160 g
GC Stellavest 8kg (4x2kg) phosphate investment
Graphite-free phosphate investment for a fast and controlled annealing process for base metals.
Especially recommended for a quick heating process without rings.
Packaging:
- 2x4kg
Sherafina 2000 160g carton 38 pieces
SHERAFINA 2000
Refractory mass for crowns and bridges:
- excellent quality;
- for injection porcelain;
- for alloys of precious and base metals;
- easy expansion control;
- for quick and slow heating;
- very fine-grained and compact consistency;
- smooth surface of castings;
- very high casting accuracy.
Packaging:
- Cardboard 38x160 g
Sherafina Rapid 160g carton 38 pieces
SHERAFINA-RAPID investment material for crowns and bridges.
Characteristics:
- for alloys of precious and base metals;
- easy expansion control;
- for quick and slow heating;
- very fine-grained and compact consistency;
- smooth surface of castings;
- very high casting accuracy.
Packaging:
- Cardboard 38x160 g