Highly aesthetic multilayer zircon for universal use. Thanks to increased strength (1000MPa), it allows for the production of multi-unit bridges, while maintaining high aesthetics of the restoration (high translucency of 47%)

Technical data:

• Strength after sintering> 1000 MPa
• Translucency 47%
• Sintering temperature 1480 ° C.

Application:

• substructures
• crowns
• 3-point bridges
• the bridge with the note

Package:

• 1 piece.

Highly aesthetic multilayer zircon for universal use. Thanks to increased strength (1000MPa), it allows for the production of multi-unit bridges, while maintaining high aesthetics of the restoration (high translucency of 47%)

Technical data:

• Strength after sintering> 1000 MPa
• Translucency 47%
• Sintering temperature 1480C

Application:

• substructures,
• crowns,
• 3-point bridges,
• a bridge with a note,

Package:

• 1 piece.

Highly aesthetic multilayer zircon for universal use. Thanks to increased strength (1000MPa), it allows for the production of multi-unit bridges, while maintaining high aesthetics of the restoration (high translucency of 47%)

Technical data:

• Strength after sintering> 1000 MPa
• Translucency 47%
• Sintering temperature 1480C

Application:

• substructures,
• crowns,
• 3-point bridges,
• a bridge with a note,

Package:

• 1 piece.

Highly aesthetic multilayer zircon for universal use. Thanks to increased strength (1000MPa), it allows for the production of multi-unit bridges, while maintaining high aesthetics of the restoration (high translucency of 47%)

Technical data:

• Strength after sintering> 1000 MPa
• Translucency 47%
• Sintering temperature 1480 ° C.

Application:

• substructures
• crowns
• 3-point bridges
• the bridge with the note

Package:

• 1 piece.

Highly aesthetic multilayer zircon for universal use. Thanks to increased strength (1000MPa), it allows for the production of multi-unit bridges, while maintaining high aesthetics of the restoration (high translucency of 47%)

Technical data:

• Strength after sintering> 1000 MPa
• Translucency 47%
• Sintering temperature 1480C

Application:

• substructures
• crowns
• 3-point bridges
• the bridge with the note

Package:

• 1 piece.

Highly aesthetic multilayer zircon for universal use. Thanks to increased strength (1000MPa), it allows for the production of multi-unit bridges, while maintaining high aesthetics of the restoration (high translucency of 47%)

Technical data:

• Strength after sintering> 1000 MPa
• Translucency 47%
• Sintering temperature 1480C

Application:

• substructures
• crowns
• 3-point bridges
• the bridge with the note

Package:

1 piece.

Highly aesthetic multilayer zircon for universal use. Thanks to increased strength (1000MPa), it allows for the production of multi-unit bridges, while maintaining high aesthetics of the restoration (high translucency of 47%)

Technical data:

• Strength after sintering> 1000 MPa
• Translucency 47%
• Sintering temperature 1480 ° C.

Application:

• substructures
• crowns
• 3-point bridges
• the bridge with the note

Package:

1 piece.

Highly aesthetic multilayer zircon for universal use. Thanks to increased strength (1000MPa), it allows for the production of multi-unit bridges, while maintaining high aesthetics of the restoration (high translucency of 47%)

Technical data:

• Strength after sintering> 1000 MPa
• Translucency 47%
• Sintering temperature 1480 ° C.

Application:

• substructures
• crowns
• 3-point bridges
• the bridge with the note

Package:

1 piece.