Kerox- Zirconium disc HT 98x12 mm Promotion
Kerox Dental zirconium blocks are made of Yttria material with a perfectly stabilized structure, manufactured by the Japanese industry leader.
Chemical properties:
- composition:
- ZrO2> 94.2%
- Y2O3 - 5.20%
- Al2O3 - 0.25%
- HfO2 <0.30%
- SiO2 <0.02%
- Fe2O3 <0.01%
- Na2O <0.04% Physical properties
- properties after sintering:
- Density (g / cm3) - 6.05
- Bending strength (MPa) - 1500
- Hardness (HV10) - 1250
- Radioactivity (Bq / g) - <0.01
Highly translucent Kerox Dental blocks with exceptional light transmission and high strength at the same time. Compared to standard zirconium, they transmit 25% more light, ensuring the best possible, natural aesthetic effect expected by patients.
Benefits:
Extraordinary aesthetic parameters Highest level of translucency Standard sintering method No need to adjust sintering parameters or furnace settings Blocks available in standard sizes Thickness 12-20 mm Best shrinkage available on the market For bridges and full prosthetic restorations Bending strength up to 1500 MPa.
Package:
1 piece.
Kerox - HT 98 X16 mm zirconium disc Promotion
Kerox Dental zirconium blocks are made of Yttria material with a perfectly stabilized structure, manufactured by the Japanese industry leader.
Chemical properties:
- composition:
- ZrO2> 94.2%
- Y2O3 - 5.20%
- Al2O3 - 0.25%
- HfO2 <0.30%
- SiO2 <0.02%
- Fe2O3 <0.01%
- Na2O <0.04% Physical properties
- properties after sintering:
- Density (g / cm3) - 6.05
- Bending strength (MPa) - 1500
- Hardness (HV10) - 1250
- Radioactivity (Bq / g) - <0.01
Highly translucent Kerox Dental blocks with exceptional light transmission and high strength at the same time. Compared to standard zirconium, they transmit 25% more light, ensuring the best possible, natural aesthetic effect expected by patients.
Advantages:
Extraordinary aesthetic parameters Highest level of translucency Standard sintering method No need to adjust sintering parameters or furnace settings Blocks available in standard sizes Thickness 12-20 mm Best shrinkage available on the market For bridges and full prosthetic reconstructions Bending strength up to 1500 MPa.
Package:
1 piece.
Kerox - zirconium disc HS 98 X25 mm Promotion
Kerox Dental zirconium blocks are made of Yttria material with a perfectly stabilized structure, manufactured by the Japanese industry leader.
Chemical properties:
- composition:
- ZrO2> 94.2%
- Y2O3 - 5.20%
- Al2O3 - 0.25%
- HfO2 <0.30%
- SiO2 <0.02%
- Fe2O3 <0.01%
- Na2O <0.04% Physical properties
- properties after sintering:
- Density (g / cm3) - 6.05
- Bending strength (MPa) - 1500
- Hardness (HV10) - 1250
- Radioactivity (Bq / g) - <0.01
HS Kerox Dental zirconium discs have the highest flexural strength on the market. A thin layer of zirconium additionally strengthens the prosthetic abutment and masks its metallic color.
Advantages:
- Unique aesthetic qualities
- High level of translucency
- Standard snterization can be used
- It is not necessary to change sintering parameters and furnace settings
- Available in standard sizes
Package:
1 piece
Kerox - HTML Zirconium Disc 98x14 mm
Characteristics :
Kerox - HT Myltilayer zircon disc
Features:
high translucency multilayer zirconia disc.
6 layers of natural gradient from neck to incisal
high translucency for a natural aesthetic
large mechanical strength
perfect shrinkage
compatible with most Cad / Cam systems
Usage:
full-contour crowns
full-contour bridges up to 3 points
Dimensions:
98x14mm
Available color:
A2, A3, B1, C2, D2
Package: 1pc.
Hyramic Upcera HT18x14x12
Hybrid ceramics with a double ceramic structure from 55% to 85% and a polymeric material from 13% to 43%. Adhesive cementation. HT translucency level.
Characteristics:
- compatible with technical CAD / CAM systems and office machines
- available in single color and multilayer (polychromatic) versions
- biocompatible.
Application:
- thin veneers
- veneers
- inlay
- onlay
- crowns
Package:
1 piece