Mesa Magnum Solare Co-Cr disk 98.5x20mm
Mesa

195.59€ +vat234.71€

211.24€ incl tax

Mesa Magnum Solare Co-Cr disk 98.5x20mm

MAGNUM SOLARE 98.5x20mm Co-Cr disc for milling ceramic-veneered crowns and bridges.

Advantages:

  • lower hardness 255 HV10 which facilitates milling and reduces wear of cutters;
  • clean oxidation;
  • coefficient of thermal expansion appropriate for most ceramic materials.

Composition in %:

  • What 66;
  • Cr 27;
  • Mo 6;
  • Si,Mn 1.

Technical data:

  • melting point 1307°C - 1417 °C;
  • thermal expansion coefficient - (25- 500 °C) 14.3 x10- 6K- 1 - (25- 600°C) 14.5x10- 6K- 1;
  • density - 8.4g/cm3;
  • Vickers hardness 255 HV10;
  • percentage elongation at break 11%;
  • unit yield strength - 395 Mpa;
  • modulus of elasticity 233 GPa.

Packaging:

  • 1pc.

Product Code: 898
Brands Mesa
Mesa Magnum Solare Co-Cr disk 98.5x20mm

195.59€ +vat234.71€

211.24€ incl tax

Product Code: 4763
Qty: 9
Mesa ERGAL Test disk 98.5x20mm
Mesa

24.24€ +vat33.13€

29.81€ incl tax

Mesa ERGAL Test disk 98.5x20mm

New ERGAL discs for test work and fittings.

It is an alloy (aluminum with zinc, magnesium and copper and trace additions of other metals).

Due to its excellent milling performance, this alloy is ideal for the production of test pieces.

It guarantees extremely high precision and at the same time extreme ease of execution.

Packaging:

  • 1pc.

Product Code: 4763
Brands Mesa
Mesa ERGAL Test disk 98.5x20mm

24.24€ +vat33.13€

29.81€ incl tax

Product Code: 5852
Qty: 10
Mesa ERGAL Test disk 98.5x16mm
Mesa

24.24€ +vat33.13€

29.81€ incl tax

Mesa ERGAL Test disk 98.5x16mm

New ERGAL discs for test work and fittings.

It is an alloy (aluminum with zinc, magnesium and copper and trace additions of other metals).

Due to its excellent milling performance, this alloy is ideal for the production of test pieces.

It guarantees extremely high precision and at the same time extreme ease of execution.

Packaging:

  • 1pc.

Product Code: 5852
Brands Mesa
Mesa ERGAL Test disk 98.5x16mm

24.24€ +vat33.13€

29.81€ incl tax

Product Code: 11303
Qty: 2
Realloy BC milling disc CoCr 98.5x14mm
Realloy E.K.

158.59€ +vat

171.28€ incl tax

Realloy BC milling disc CoCr 98.5x14mm

Milling disc from the German company Realloy.

Characteristics:

  • diameter 98.5 mm compatible with most milling machines;
  • alloy for veneering with ceramics.

Technical data:

  • hardness (HV) 290;
  • elongation (%) 8;
  • tensile strength(MPa) 560;
  • elastic limit (MPa) at elongation.0.2% 400;
  • modulus of elasticity (GPa) approx. 195;
  • thermal expansion coefficient (20'- 6000c) (10K) 14.1- 14.4;
  • density (g/cm') 8.4.

Composition:

  • What (%) 61.7;
  • Cr |%) 27.8;
  • Si(%) 1.6;
  • In (%) 8.5;
  • other(%) <1.

Packaging:

  • 1pc.

Product Code: 11303
Realloy BC milling disc CoCr 98.5x14mm

158.59€ +vat

171.28€ incl tax

Product Code: 11304
Qty: 3
Realloy BC Milling Disc CoCr 98.5x10mm
Realloy E.K.

134.66€ +vat

145.43€ incl tax

Realloy BC Milling Disc CoCr 98.5x10mm

Milling disc from the German company Realloy.

Characteristics:

  • diameter 98.5 mm compatible with most milling machines;
  • alloy for veneering with ceramics.

Technical data:

  • hardness (HV) 290;
  • elongation (%) 8;
  • tensile strength(MPa) 560;
  • elastic limit (MPa) at elongation.0.2% 400;
  • modulus of elasticity (GPa) approx. 195;
  • thermal expansion coefficient (20'- 6000c) (10K) 14.1- 14.4;
  • density (g/cm') 8.4.

Composition:

  • What (%) 61.7;
  • Cr |%) 27.8;
  • Si(%) 1.6;
  • In (%) 8.5;
  • other(%) <1.

Packaging:

  • 1pc.

Product Code: 11304
Realloy BC Milling Disc CoCr 98.5x10mm

134.66€ +vat

145.43€ incl tax

Product Code: 11305
Qty: 1
Realloy BC Milling Disc CoCr 98.5x12mm
Realloy E.K.

145.75€ +vat

157.41€ incl tax

Realloy BC Milling Disc CoCr 98.5x12mm

Milling disc from the German company Realloy.

Characteristics:

  • diameter 98.5 mm compatible with most milling machines;
  • alloy for veneering with ceramics.

Technical data:

  • hardness (HV) 290;
  • elongation (%) 8;
  • tensile strength(MPa) 560;
  • elastic limit (MPa) at elongation.0.2% 400;
  • modulus of elasticity (GPa) approx. 195;
  • thermal expansion coefficient (20'- 6000c) (10K) 14.1- 14.4;
  • density (g/cm') 8.4.

Composition:

  • What (%) 61.7;
  • Cr |%) 27.8;
  • Si(%) 1.6;
  • In (%) 8.5;
  • other(%) <1.

Packaging:

  • 1pc.

Product Code: 11305
Realloy BC Milling Disc CoCr 98.5x12mm

145.75€ +vat

157.41€ incl tax

Product Code: 11306
Qty: 1
Realloy BC milling disc CoCr 98.5x13.5mm
Realloy E.K.

156.63€ +vat

169.16€ incl tax

Realloy BC milling disc CoCr 98.5x13.5mm

Milling disc from the German company Realloy.

Characteristics:

  • diameter 98.5 mm compatible with most milling machines;
  • alloy for veneering with ceramics.

Technical data:

  • hardness (HV) 290;
  • elongation (%) 8;
  • tensile strength(MPa) 560;
  • elastic limit (MPa) at elongation.0.2% 400;
  • modulus of elasticity (GPa) approx. 195;
  • thermal expansion coefficient (20'- 6000c) (10K) 14.1- 14.4;
  • density (g/cm') 8.4.

Composition:

  • What (%) 61.7;
  • Cr |%) 27.8;
  • Si(%) 1.6;
  • In (%) 8.5;
  • other(%) <1.

Packaging:

  • 1pc.

Product Code: 11306
Realloy BC milling disc CoCr 98.5x13.5mm

156.63€ +vat

169.16€ incl tax

Product Code: 11970
Qty: 5
Mesa Magnum Splendidum Co-Cr disk 98.5x10mm
Mesa

119.82€ +vat143.79€

129.41€ incl tax

Mesa Magnum Splendidum Co-Cr disk 98.5x10mm

MAGNUM SPLENDIDUM 98x10mm Co-Cr disc for milling crowns and bridges veneered with ceramic.

Advantages:

  • excellent polishing results;
  • coefficient of thermal expansion appropriate for most ceramic materials.

Composition in %;

  • Every 60;
  • Cr 28;
  • In 9;
  • Si1.5;
  • Mn,Fe 1.5.

Technical data:

  • melting point 1308 - 1384 °C;
  • thermal expansion coefficient - (25- 500 0176°C) 14.2 x10- 6K- 1 - (25- 600°C) 14.4x10- 6K- 1;
  • density - 8.5g/cm3;
  • Vickers hardness 273 HV10;
  • percentage elongation at break 16%;
  • unit yield strength - 360 Mpa;
  • modulus of elasticity 183 GPa.

Packaging:

  • 1pc

Product Code: 11970
Brands Mesa
Mesa Magnum Splendidum Co-Cr disk 98.5x10mm

119.82€ +vat143.79€

129.41€ incl tax

Product Code: 11971
Qty: 5
Mesa Magnum Splendidum Co-Cr disc 98.5x12mm
Mesa

126.48€ +vat151.78€

136.60€ incl tax

Mesa Magnum Splendidum Co-Cr disc 98.5x12mm

MAGNUM SPLENDIDUM 98.5x12mm Co-Cr disc for milling crowns and bridges veneered with ceramic.

Advantages:

  • excellent polishing results;
  • coefficient of thermal expansion appropriate for most ceramic materials.

Composition in %;

  • Every 60;
  • Cr 28;
  • In 9;
  • Si1.5;
  • Mn,Fe 1.5.

Technical data:

  • melting point 1308- 1384 °C;
  • thermal expansion coefficient - (25- 500 °C) 14.2 x10- 6K- 1 - (25- 600°C) 14.4x10- 6K- 1;
  • density - 8.5g/cm3;
  • Vickers hardness 273 HV10;
  • percentage elongation at break 16%;
  • unit yield strength - 360 Mpa;
  • modulus of elasticity 183 GPa.

Packaging:

  • 1pc.

Product Code: 11971
Brands Mesa
Mesa Magnum Splendidum Co-Cr disc 98.5x12mm

126.48€ +vat151.78€

136.60€ incl tax

Product Code: 11972
Qty: 6
Mesa Magnum Splendidum Co-Cr disc 98.5x13.5mm
Mesa

136.07€ +vat163.29€

146.96€ incl tax

Mesa Magnum Splendidum Co-Cr disc 98.5x13.5mm

MAGNUM SPLENDIDUM 98.5x13.5mm Co-Cr disc for milling crowns and bridges veneered with ceramic.

Advantages:

  • excellent polishing results;
  • coefficient of thermal expansion appropriate for most ceramic materials.

Composition in %:

  • Every 60;
  • Cr 28;
  • In 9;
  • Si1.5;
  • Mn,Fe 1.5.

Technical data:

  • melting point 1308- 1384 °C;
  • thermal expansion coefficient - (25- 500°C) 14.2 x10- 6K- 1 - (25- 600°C) 14.4x10- 6K- 1;
  • density - 8.5g/cm3;
  • Vickers hardness 273 HV10;
  • percentage elongation at break 16%;
  • unit yield strength - 360 Mpa;
  • modulus of elasticity 183 GPa.

Packaging:

  • 1pc.

Product Code: 11972
Brands Mesa
Mesa Magnum Splendidum Co-Cr disc 98.5x13.5mm

136.07€ +vat163.29€

146.96€ incl tax

Product Code: 11973
Qty: 2
Mesa Magnum Splendidum disc Co-Cr 98.5x15mm
Mesa

144.69€ +vat173.63€

156.26€ incl tax

Mesa Magnum Splendidum disc Co-Cr 98.5x15mm

MAGNUM SPLENDIDUM 98.5x15mm Co-Cr disc for milling crowns and bridges veneered with ceramic.

Advantages:

  • excellent polishing results;
  • coefficient of thermal expansion appropriate for most ceramic materials.

Composition in %:

  • Every 60;
  • Cr 28;
  • In 9;
  • Si1.5;
  • Mn,Fe 1.5.

Technical data:

  • melting point 1308 - 1384 °C;
  • thermal expansion coefficient - (25- 500°C) 14.2 x10- 6K- 1 - (25- 600°C) 14.4x10- 6K- 1;
  • density - 8.5g/cm3;
  • Vickers hardness 273 HV10;
  • percentage elongation at break 16%;
  • unit yield strength - 360 Mpa;
  • modulus of elasticity 183 GPa.

Packaging:

  • 1pc.

Product Code: 11973
Brands Mesa
Mesa Magnum Splendidum disc Co-Cr 98.5x15mm

144.69€ +vat173.63€

156.26€ incl tax

Product Code: 11974
Qty: 3
Mesa Magnum Splendidum Co-Cr disc 98.5x16mm
Mesa

159.57€ +vat191.48€

172.33€ incl tax

Mesa Magnum Splendidum Co-Cr disc 98.5x16mm

MAGNUM SPLENDIDUM 98.5x16mm Co-Cr disc for milling crowns and bridges veneered with ceramic.

Advantages:

  • excellent polishing results;
  • coefficient of thermal expansion appropriate for most ceramic materials.

Composition in %:

  • Every 60;
  • Cr 28;
  • In 9;
  • Si1.5;
  • Mn,Fe 1.5.

Technical data:

  • melting point 1308 - 1384 °C;
  • thermal expansion coefficient - (25- 500°C) 14.2 x10- 6K- 1 - (25- 600°C) 14.4x10- 6K- 1;
  • density - 8.5g/cm3;
  • Vickers hardness 273 HV10;
  • percentage elongation at break 16%;
  • unit yield strength - 360 Mpa;
  • modulus of elasticity 183 GPa.

Packaging:

  • 1pc.

Product Code: 11974
Brands Mesa
Mesa Magnum Splendidum Co-Cr disc 98.5x16mm

159.57€ +vat191.48€

172.33€ incl tax

Product Code: 11975
Qty: 1
Mesa Magnum Splendidum Co-Cr disc 98.5x18mm
Mesa

166.81€ +vat200.17€

180.16€ incl tax

Mesa Magnum Splendidum Co-Cr disc 98.5x18mm

MAGNUM SPLENDIDUM 98.5x18mm Co-Cr disc for milling crowns and bridges veneered with ceramic.

Advantages:

  • excellent polishing results;
  • coefficient of thermal expansion appropriate for most ceramic materials.

Composition in %:

  • Every 60;
  • Cr 28;
  • In 9;
  • Si1.5;
  • Mn,Fe 1.5.

Technical data:

  • melting point 1308 - 1384 °C;
  • thermal expansion coefficient - (25- 500°C) 14.2 x10- 6K- 1 - (25- 600°C) 14.4x10- 6K- 1;
  • density - 8.5g/cm3;
  • Vickers hardness 273 HV10;
  • percentage elongation at break 16%;
  • unit yield strength - 360 Mpa;
  • modulus of elasticity 183 GPa.

Packaging:

  • 1pc.

Product Code: 11975
Brands Mesa
Mesa Magnum Splendidum Co-Cr disc 98.5x18mm

166.81€ +vat200.17€

180.16€ incl tax

Product Code: 12657
Qty: 4
Mesa Magnum Splendidum disc Co-Cr 98.5x14mm
Mesa

142.93€ +vat171.51€

154.36€ incl tax

Mesa Magnum Splendidum disc Co-Cr 98.5x14mm

MAGNUM SPLENDIDUM 98.5x14mm Co-Cr disc for milling crowns and bridges veneered with ceramic.

Advantages:

  • excellent polishing results;
  • coefficient of thermal expansion appropriate for most ceramic materials.

Composition in %:

  • Every 60;
  • Cr 28;
  • In 9;
  • Si1.5;
  • Mn,Fe 1.5.

Technical data:

  • melting point 1308 - 1384 °C;
  • thermal expansion coefficient - (25- 500°C) 14.2 x10- 6K- 1 - (25- 600°C) 14.4x10- 6K- 1;
  • density - 8.5g/cm3;
  • Vickers hardness 273 HV10;
  • percentage elongation at break 16%;
  • unit yield strength - 360 Mpa;
  • modulus of elasticity 183 GPa.

Packaging:

  • 1pc.

Product Code: 12657
Brands Mesa
Mesa Magnum Splendidum disc Co-Cr 98.5x14mm

142.93€ +vat171.51€

154.36€ incl tax

Product Code: 13114
Qty: 2
Mesa Magnum Splendidum disc Co-Cr 98.5x8mm
Mesa

111.40€ +vat133.68€

120.32€ incl tax

Mesa Magnum Splendidum disc Co-Cr 98.5x8mm

MAGNUM SPLENDIDUM 98.5x8mm Co-Cr disc for milling crowns and bridges veneered with ceramic.

Advantages:

  • excellent polishing results;
  • coefficient of thermal expansion appropriate for most ceramic materials.

Composition in %:

  • Every 60;
  • Cr 28;
  • In 9;
  • Si1.5;
  • Mn,Fe 1.5.

Technical data:

  • melting point 1308 - 1384 °C;
  • thermal expansion coefficient - (25- 500°C) 14.2 x10- 6K- 1 - (25- 600°C) 14.4x10- 6K- 1;
  • density - 8.5g/cm3;
  • Vickers hardness 273 HV10;
  • percentage elongation at break 16%;
  • unit yield strength - 360 Mpa;
  • modulus of elasticity 183 GPa.

Packaging:

  • 1pc.

Product Code: 13114
Brands Mesa
Mesa Magnum Splendidum disc Co-Cr 98.5x8mm

111.40€ +vat133.68€

120.32€ incl tax

Product Code: 14126
Qty: 2
Realloy BC Milling Disc CoCr 98.5x16mm
Realloy E.K.

165.77€ +vat

179.03€ incl tax

Realloy BC Milling Disc CoCr 98.5x16mm

Milling disc from the German company Realloy.

Characteristics:

  • diameter 98.5 mm compatible with most milling machines;
  • alloy for veneering with ceramics.

Technical data:

  • hardness (HV) 290;
  • elongation (%) 8;
  • tensile strength(MPa) 560;
  • elastic limit (MPa) at elongation.0.2% 400;
  • modulus of elasticity (GPa) approx. 195;
  • thermal expansion coefficient (20'- 6000c) (10K) 14.1- 14.4;
  • density (g/cm') 8.4.

Composition:

  • What (%) 61.7;
  • Cr |%) 27.8;
  • Si(%) 1.6;
  • In (%) 8.5;
  • other(%) <1.

Packaging:

  • 1pc.

Product Code: 14126
Realloy BC Milling Disc CoCr 98.5x16mm

165.77€ +vat

179.03€ incl tax

Product Code: 14127
Qty: 1
Realloy BC milling disc CoCr 98.5x18mm
Realloy E.K.

181.65€ +vat

196.18€ incl tax

Realloy BC milling disc CoCr 98.5x18mm

Milling disc from the German company Realloy.

Characteristics:

  • diameter 98.5 mm compatible with most milling machines;
  • alloy for veneering with ceramics.

Technical data:

  • hardness (HV) 290;
  • elongation (%) 8;
  • tensile strength(MPa) 560;
  • elastic limit (MPa) at elongation.0.2% 400;
  • modulus of elasticity (GPa) approx. 195;
  • thermal expansion coefficient (20'- 6000c) (10K) 14.1- 14.4;
  • density (g/cm') 8.4.

Composition:

  • What (%) 61.7;
  • Cr |%) 27.8;
  • Si(%) 1.6;
  • In (%) 8.5;
  • other(%) <1.

Packaging:

  • 1pc.

Product Code: 14127
Realloy BC milling disc CoCr 98.5x18mm

181.65€ +vat

196.18€ incl tax

Product Code: 14405
Qty: 2
Realloy BC milling disc CoCr 98.5x15mm
Realloy E.K.

161.63€ +vat

174.56€ incl tax

Realloy BC milling disc CoCr 98.5x15mm

Milling disc from the German company Realloy.

Characteristics:

  • diameter 98.5 mm compatible with most milling machines;
  • alloy for veneering with ceramics.

Technical data:

  • hardness (HV) 290;
  • elongation (%) 8;
  • tensile strength(MPa) 560;
  • elastic limit (MPa) at elongation.0.2% 400;
  • modulus of elasticity (GPa) approx. 195;
  • thermal expansion coefficient (20'- 6000c) (10K) 14.1- 14.4;
  • density (g/cm') 8.4.

Composition:

  • What (%) 61.7;
  • Cr |%) 27.8;
  • Si(%) 1.6;
  • In (%) 8.5;
  • other(%) <1.

Packaging:

  • 1pc.

Product Code: 14405
Realloy BC milling disc CoCr 98.5x15mm

161.63€ +vat

174.56€ incl tax

Product Code: 14734
Qty: 1
Realloy BC milling disc CoCr 98.5x8mm
Realloy E.K.

132.70€ +vat

143.32€ incl tax

Realloy BC milling disc CoCr 98.5x8mm

Milling disc from the German company Realloy.

Characteristics:

  • diameter 98.5 mm compatible with most milling machines;
  • alloy for veneering with ceramics.

Technical data:

  • hardness (HV) 290;
  • elongation (%) 8;
  • tensile strength(MPa) 560;
  • elastic limit (MPa) at elongation.0.2% 400;
  • modulus of elasticity (GPa) approx. 195;
  • thermal expansion coefficient (20'- 6000c) (10K) 14.1- 14.4;
  • density (g/cm') 8.4.

Composition:

  • What (%) 61.7;
  • Cr |%) 27.8;
  • Si(%) 1.6;
  • In (%) 8.5;
  • other(%) <1.

Packaging:

  • 1pc.

Product Code: 14734
Realloy BC milling disc CoCr 98.5x8mm

132.70€ +vat

143.32€ incl tax

Product Code: 14894
Qty: 3
Mesa Magnum Solare Co-Cr disk 98.5x10mm
Mesa

119.82€ +vat143.79€

129.41€ incl tax

Mesa Magnum Solare Co-Cr disk 98.5x10mm

MAGNUM SOLARE 98.5x10mm Co-Cr disc for milling ceramic-veneered crowns and bridges.

Advantages:

  • lower hardness 255 HV10 which facilitates milling and reduces wear of cutters;
  • clean oxidation;
  • coefficient of thermal expansion appropriate for most ceramic materials.

Composition in %:

  • What 66;
  • Cr 27;
  • Mo 6;
  • Si,Mn 1.

Technical data:

  • melting point 1307°C - 1417 °C;
  • thermal expansion coefficient - (25- 500 °C) 14.3 x10- 6K- 1 - (25- 600°C) 14.5x10- 6K- 1;
  • density - 8.4g/cm3;
  • Vickers hardness 255 HV10;
  • percentage elongation at break 11%;
  • unit yield strength - 395 Mpa;
  • modulus of elasticity 233 GPa.

Packaging:

  • 1pc.

Product Code: 14894
Brands Mesa
Mesa Magnum Solare Co-Cr disk 98.5x10mm

119.82€ +vat143.79€

129.41€ incl tax

Product Code: 14895
Qty: 4
Mesa Magnum Solare Co-Cr disk 98.5x12mm
Mesa

126.48€ +vat151.78€

136.60€ incl tax

Mesa Magnum Solare Co-Cr disk 98.5x12mm

MAGNUM SOLARE 98.5x12mm Co-Cr disc for milling ceramic-veneered crowns and bridges.

Advantages:

  • lower hardness 255 HV10 which facilitates milling and reduces wear of cutters;
  • clean oxidation;
  • coefficient of thermal expansion appropriate for most ceramic materials.

Composition in %:

  • What 66;
  • Cr 27;
  • Mo 6;
  • Si,Mn 1.

Technical data:

  • melting point 1307°C - 1417 °C;
  • thermal expansion coefficient - (25- 500 °C) 14.3 x10- 6K- 1 - (25- 600°C) 14.5x10- 6K- 1;
  • density - 8.4g/cm3;
  • Vickers hardness 255 HV10;
  • percentage elongation at break 11%;
  • unit yield strength - 395 Mpa;
  • modulus of elasticity 233 GPa.

Packaging:

  • 1pc.

Product Code: 14895
Brands Mesa
Mesa Magnum Solare Co-Cr disk 98.5x12mm

126.48€ +vat151.78€

136.60€ incl tax

Product Code: 14896
Qty: 3
Mesa Magnum Solare Co-Cr disc 98.5x13.5mm
Mesa

136.07€ +vat163.29€

146.96€ incl tax

Mesa Magnum Solare Co-Cr disc 98.5x13.5mm

MAGNUM SOLARE 98.5x13.5mm Co-Cr disc for milling crowns and bridges veneered with ceramic.

Advantages:

  • lower hardness 255 HV10 which facilitates milling and reduces wear of cutters;
  • clean oxidation;
  • coefficient of thermal expansion appropriate for most ceramic materials.

Composition in %:

  • What 66;
  • Cr 27;
  • Mo 6;
  • Si,Mn 1.

Technical data:

  • melting point 1307°C - 1417 °C;
  • thermal expansion coefficient - (25- 500 °C) 14.3 x10- 6K- 1 - (25- 600°C) 14.5x10- 6K- 1;
  • density - 8.4g/cm3;
  • Vickers hardness 255 HV10;
  • percentage elongation at break 11%;
  • unit yield strength - 395 Mpa;
  • modulus of elasticity 233 GPa.

Packaging:

  • 1pc.

Product Code: 14896
Brands Mesa
Mesa Magnum Solare Co-Cr disc 98.5x13.5mm

136.07€ +vat163.29€

146.96€ incl tax

Product Code: 14897
Qty: 1
Mesa Magnum Solare Co-Cr disc 98.5x15mm
Mesa

144.69€ +vat173.63€

156.26€ incl tax

Mesa Magnum Solare Co-Cr disc 98.5x15mm

MAGNUM SOLARE 98.5x15mm Co-Cr disc for milling ceramic-veneered crowns and bridges.

Advantages:

  • lower hardness 255 HV10 which facilitates milling and reduces wear of cutters;
  • clean oxidation;
  • coefficient of thermal expansion appropriate for most ceramic materials.

Composition in %:

  • What 66;
  • Cr 27;
  • Mo 6;
  • Si,Mn 1.

Technical data:

  • melting point 1307°C - 1417 °C;
  • thermal expansion coefficient - (25- 500 °C) 14.3 x10- 6K- 1 - (25- 600°C) 14.5x10- 6K- 1;
  • density - 8.4g/cm3;
  • Vickers hardness 255 HV10;
  • percentage elongation at break 11%;
  • unit yield strength - 395 Mpa;
  • modulus of elasticity 233 GPa.

Packaging:

  • 1pc.

Product Code: 14897
Brands Mesa
Mesa Magnum Solare Co-Cr disc 98.5x15mm

144.69€ +vat173.63€

156.26€ incl tax

Product Code: 14898
Qty: 2
Mesa Magnum Solare Co-Cr disc 98.5x18mm
Mesa

166.81€ +vat200.17€

180.16€ incl tax

Mesa Magnum Solare Co-Cr disc 98.5x18mm

MAGNUM SOLARE 98.5x18mm Co-Cr disc for milling ceramic-veneered crowns and bridges.

Advantages:

  • lower hardness 255 HV10 which facilitates milling and reduces wear of cutters;
  • clean oxidation;
  • coefficient of thermal expansion appropriate for most ceramic materials.

Composition in %:

  • What 66;
  • Cr 27;
  • Mo 6;
  • Si,Mn 1.

Technical data:

  • melting point 1307°C - 1417 °C;
  • thermal expansion coefficient - (25- 500 °C) 14.3 x10- 6K- 1 - (25- 600°C) 14.5x10- 6K- 1;
  • density - 8.4g/cm3;
  • Vickers hardness 255 HV10;
  • percentage elongation at break 11%;
  • unit yield strength - 395 Mpa;
  • modulus of elasticity 233 GPa.

Packaging:

  • 1pc.

Product Code: 14898
Brands Mesa
Mesa Magnum Solare Co-Cr disc 98.5x18mm

166.81€ +vat200.17€

180.16€ incl tax

Product Code: 15050
Qty: 6
Mesa Magnum Hyperone Ti disk 98.5x12mm
Mesa

67.55€ +vat81.06€

72.95€ incl tax

Mesa Magnum Hyperone Ti disk 98.5x12mm

MESA MAGNUM HYPERONE.

Titanium based milling discs for open systems 98.5mm from Mesa.

They are characterized by high biocompatibility.

Manufactured in accordance with ASTM F136.

The minimum construction thickness is 0.3 mm for simple structures and 0.5 mm in more complex cases or in patients with bruxism.

Avoid sharp angles.

Separate the milled structures from the disc using tungsten carbide burs or titanium grinding wheels.

Clean with acetone or bioalcohol to eliminate any greasy contamination.

Once the treatment is complete, the product should be sandblasted with 110 to 150 micron aluminium oxide at a maximum pressure of 2-3 bar and then steam cleaned.

After cleaning, the product should be handled with tongs.

Chemical composition:

  • Ti 90%;
  • Al 6%;
  • V 4%;
  • Fe remaining;

Physical and mechanical properties:

  • density : 4.426 g/cm3;
  • melting point: 1605- 1660 °C;
  • melting point: 1710 °C;
  • unit yield strength: 880 MPa;
  • percentage elongation at break: 14%;
  • modulus of elasticity: 114 GPa;
  • Vickers hardness: 312 HV10.

Packaging:

  • 1pc.

Product Code: 15050
Brands Mesa
Mesa Magnum Hyperone Ti disk 98.5x12mm

67.55€ +vat81.06€

72.95€ incl tax

Product Code: 15051
Qty: 11
Mesa Magnum Hyperone Ti disk 98.5x10mm
Mesa

56.58€ +vat67.90€

61.11€ incl tax

Mesa Magnum Hyperone Ti disk 98.5x10mm

MESA MAGNUM HYPERONE.

Titanium based milling discs for open systems 98.5mm from Mesa.

They are characterized by high biocompatibility.

Manufactured in accordance with ASTM F136.

The minimum construction thickness is 0.3 mm for simple structures and 0.5 mm in more complex cases or in patients with bruxism.

Avoid sharp angles.

Separate the milled structures from the disc using tungsten carbide burs or titanium grinding wheels.

Clean with acetone or bioalcohol to eliminate any greasy contamination.

Once the treatment is complete, the product should be sandblasted with 110 to 150 micron aluminium oxide at a maximum pressure of 2-3 bar and then steam cleaned.

After cleaning, the product should be handled with tongs.

Chemical composition:

  • Ti 90%;
  • Al 6%;
  • V 4%;
  • Fe remaining;

Physical and mechanical properties:

  • density : 4.426 g/cm3;
  • melting point: 1605- 1660 °C;
  • melting point: 1710 °C;
  • unit yield strength: 880 MPa;
  • percentage elongation at break: 14%;
  • modulus of elasticity: 114 GPa;
  • Vickers hardness: 312 HV10.

Packaging:

  • 1pc.

Product Code: 15051
Brands Mesa
Mesa Magnum Hyperone Ti disk 98.5x10mm

56.58€ +vat67.90€

61.11€ incl tax

Product Code: 15052
Qty: 7
Mesa Magnum Hyperone Ti disk 98.5x13.5mm
Mesa

74.79€ +vat89.75€

80.77€ incl tax

Mesa Magnum Hyperone Ti disk 98.5x13.5mm

MESA MAGNUM HYPERONE.

Titanium based milling discs for open systems 98.5mm from Mesa.

They are characterized by high biocompatibility.

Manufactured in accordance with ASTM F136.

The minimum construction thickness is 0.3 mm for simple structures and 0.5 mm in more complex cases or in patients with bruxism.

Avoid sharp angles.

Separate the milled structures from the disc using tungsten carbide burs or titanium grinding wheels.

Clean with acetone or bioalcohol to eliminate any greasy contamination.

Once the treatment is complete, the product should be sandblasted with 110 to 150 micron aluminium oxide at a maximum pressure of 2-3 bar and then steam cleaned.

After cleaning, the product should be handled with tongs.

Chemical composition:

  • Ti 90%;
  • Al 6%;
  • V 4%;
  • Fe remaining;

Physical and mechanical properties:

  • density : 4.426 g/cm3;
  • melting point: 1605- 1660 °C;
  • melting point: 1710 °C;
  • unit yield strength: 880 MPa;
  • percentage elongation at break: 14%;
  • modulus of elasticity: 114 GPa;
  • Vickers hardness: 312 HV10.

Packaging:

  • 1pc.

Product Code: 15052
Brands Mesa
Mesa Magnum Hyperone Ti disk 98.5x13.5mm

74.79€ +vat89.75€

80.77€ incl tax

Product Code: 15053
Qty: 2
Mesa Magnum Hyperone Ti disk 98.5x15mm
Mesa

80.86€ +vat97.03€

87.33€ incl tax

Mesa Magnum Hyperone Ti disk 98.5x15mm

MESA MAGNUM HYPERONE.

Titanium based milling discs for open systems 98.5mm from Mesa.

They are characterized by high biocompatibility.

Manufactured in accordance with ASTM F136.

The minimum construction thickness is 0.3 mm for simple structures and 0.5 mm in more complex cases or in patients with bruxism.

Avoid sharp angles.

Separate the milled structures from the disc using tungsten carbide burs or titanium grinding wheels.

Clean with acetone or bioalcohol to eliminate any greasy contamination.

Once the treatment is complete, the product should be sandblasted with 110 to 150 micron aluminium oxide at a maximum pressure of 2-3 bar and then steam cleaned.

After cleaning, the product should be handled with tongs.

Chemical composition:

  • Ti 90%;
  • Al 6%;
  • V 4%;
  • Fe remaining;

Physical and mechanical properties:

  • density : 4.426 g/cm3;
  • melting point: 1605- 1660 °C;
  • melting point: 1710 °C;
  • unit yield strength: 880 MPa;
  • percentage elongation at break: 14%;
  • modulus of elasticity: 114 GPa;
  • Vickers hardness: 312 HV10.

Packaging:

  • 1pc.

Product Code: 15053
Brands Mesa
Mesa Magnum Hyperone Ti disk 98.5x15mm

80.86€ +vat97.03€

87.33€ incl tax

Product Code: 15672
Qty: Only on request
Copra Sintec Evo K CoCr
Whitepeaks

154.89€ +vat

167.28€ incl tax

Copra Sintec Evo K CoCr

The world's first 98mm diameter "medium-soft" Co/Cr milling discs - wet or dry!

The material is pre-sintered, which allows for more delicate structures and minimal wall thicknesses.

The disc no longer contains a binder, so the sintering time is significantly reduced, resulting in lower argon gas consumption.

Produced in an isostatic high-pressure process.

Very little drill wear.

Sizes:

  • 98x12mm
  • 98x14mm

Packaging:

  • 1pc

Product Code: 15672
Brands Whitepeaks
Copra Sintec Evo K CoCr

154.89€ +vat

167.28€ incl tax

Product Code: 15674
Qty: Only on request
Copra Sintec K CoCr
Whitepeaks

185.13€ +vat

199.94€ incl tax

Copra Sintec K CoCr

Wax-soft Co/Cr milling discs - wet or dry! The isostatic high-pressure manufacturing process allows for the creation of bridges with up to 14 units and even implant restorations.

Type 4 base metal alloy so there are no limitations compared to milled or cast Co/Cr alloys.

Low shrinkage allows for up to 40 pieces to be placed in a semi-finished product.

Minimal drill wear.

Sizes:

  • 98x12mm
  • 98x14mm

Packaging:

  • 1pc

Product Code: 15674
Brands Whitepeaks
Copra Sintec K CoCr

185.13€ +vat

199.94€ incl tax

Product Code: 15738
Qty: 2-3 Days
MESA Magnum Solare Co-Cr disc 98.5x16mm
Mesa

159.57€ +vat191.48€

172.33€ incl tax

MESA Magnum Solare Co-Cr disc 98.5x16mm

MAGNUM SOLARE 98.5x16mm Co-Cr disc for milling ceramic-veneered crowns and bridges.

Advantages:

  • lower hardness 255 HV10 which facilitates milling and reduces wear of cutters;
  • clean oxidation;
  • coefficient of thermal expansion appropriate for most ceramic materials.

Composition in %:

  • What 66;
  • Cr 27;
  • Mo 6;
  • Si,Mn 1.

Technical data:

  • melting point 1307°C - 1417 °C;
  • thermal expansion coefficient - (25- 500 °C) 14.3 x10- 6K- 1 - (25- 600°C) 14.5x10- 6K- 1;
  • density - 8.4g/cm3;
  • Vickers hardness 255 HV10;
  • percentage elongation at break 11%;
  • unit yield strength - 395 Mpa;
  • modulus of elasticity 233 GPa.

Packaging:

  • 1pc

Product Code: 15738
Brands Mesa
MESA Magnum Solare Co-Cr disc 98.5x16mm

159.57€ +vat191.48€

172.33€ incl tax

Product Code: 15967
Qty: 1
Mesa Magnum Solare Co-Cr disc 98.5x8mm
Mesa

111.40€ +vat133.68€

120.32€ incl tax

Mesa Magnum Solare Co-Cr disc 98.5x8mm

MAGNUM SOLARE 98.5x8mm Co-Cr disc for milling ceramic-veneered crowns and bridges.

Advantages:

  • lower hardness 255 HV10 which facilitates milling and reduces wear of cutters;
  • clean oxidation;
  • coefficient of thermal expansion appropriate for most ceramic materials.

Composition in %:

  • What 66;
  • Cr 27;
  • Mo 6;
  • Si,Mn 1.

Technical data:

  • melting point 1307°C - 1417 °C;
  • thermal expansion coefficient - (25- 500 °C) 14.3 x10- 6K- 1 - (25- 600°C) 14.5x10- 6K- 1;
  • density - 8.4g/cm3;
  • Vickers hardness 255 HV10;
  • percentage elongation at break 11%;
  • unit yield strength - 395 Mpa;
  • modulus of elasticity 233 GPa.

Packaging:

  • 1pc.

Product Code: 15967
Brands Mesa
Mesa Magnum Solare Co-Cr disc 98.5x8mm

111.40€ +vat133.68€

120.32€ incl tax

Product Code: 16195
Qty: 7
Mesa Magnum Hyperone Ti disk 98.5x18mm
Mesa

87.91€ +vat105.49€

94.94€ incl tax

Mesa Magnum Hyperone Ti disk 98.5x18mm

MESA MAGNUM HYPERONE.

Titanium based milling discs for open systems 98.5mm from Mesa.

They are characterized by high biocompatibility.

Manufactured in accordance with ASTM F136.

The minimum construction thickness is 0.3 mm for simple structures and 0.5 mm in more complex cases or in patients with bruxism.

Avoid sharp angles.

Separate the milled structures from the disc using tungsten carbide burs or titanium grinding wheels.

Clean with acetone or bioalcohol to eliminate any greasy contamination.

Once the treatment is complete, the product should be sandblasted with 110 to 150 micron aluminium oxide at a maximum pressure of 2-3 bar and then steam cleaned.

After cleaning, the product should be handled with tongs.

Chemical composition:

  • Ti 90%;
  • Al 6%;
  • V 4%;
  • Fe remaining;

Physical and mechanical properties:

  • density : 4.426 g/cm3;
  • melting point: 1605- 1660 °C;
  • melting point: 1710 °C;
  • unit yield strength: 880 MPa;
  • percentage elongation at break: 14%;
  • modulus of elasticity: 114 GPa;
  • Vickers hardness: 312 HV10.

Packaging:

  • 1pc.

Product Code: 16195
Brands Mesa
Mesa Magnum Hyperone Ti disk 98.5x18mm

87.91€ +vat105.49€

94.94€ incl tax