Plaster for working models when making removable orthodontic appliances.

Characteristic:

• Low degree of linear expansion.

• Glossy white color.

• High liquidity.

Advantages:

• Smooth surface.

• Easy to prepare and process.

• Surface resistance to abrasion.

Parameters:

• White color
• Mixing proportions 30 ml / 100 g.
• Setting time 10 - 12 min.
• Linear expansion after 2 hours < 0.13%.

Packaging:

• 25kg.

Attention:

• Due to the heavy weight of the goods (25 kg), an additional fee will be added to the shipment.

Class IV Eco Stone Ortho Premium gypsum, super white, enriched with synthetic material. Very suitable for diagnostic and demonstration models, for orthodontics and under porcelain.

Parameters:

• Manual mixing time - 60 sec.
• Mixing time in a mixer - 30 sec.
• Setting time - 10 -12 minutes.
• Expansion after 2 hours - 0.14%.

Packaging:

• 25kg.

Attention:

• Due to the heavy weight of the goods (25 kg), an additional fee will be added to the shipment.

Super hard dental plaster type V, golden-brown color.

Destiny:

• Working models for making permanent dentures, combined works, post-implantation dentures.

Characteristics:

• High resistance to mechanical damage.
• Very good dimensional stability.
• Accurate reproduction of details.

Parameters:

• Golden-brown color.
• Mixing proportions 20 ml / 100 g.
• Working time 7 min.
• Setting time (at 23°C) 12-14 min.
• Linear expansion after 2 hours 0.25%.

Packaging:

• 25kg

Attention:

• Due to the heavy weight of the goods (25 kg), an additional fee will be added to the shipment.

Class IV plaster for super-hard Rubinite models, pink, natural color. Perfect for working with frames and thermal injection techniques.

Features:

• Mixing proportions: 22-24 ml/ 100 g
• Working time: 7 min.
• Setting time: 12 min
• Expansion after setting: 0.10%
• Compressive strength: 40 MPa

Attention:

• Due to the heavy weight of the goods (25 kg), an additional fee will be added to the shipment.

Packaging:

• 25kg.

High-quality modeling plaster of natural origin.

Advantages:

• Releases from the impression precisely and easily (only 20 minutes!).
• Thixotropic.
• Very high durability.
• It allows you to obtain excellent results when working with optical scanning systems.

Instructions for use:

• Powder/water ratio: 100 g / 20 ml.
• Operating temperature: 20-23 °C.
• Mechanical mixing in vacuum: 30 seconds. -Hand mixing: 60 seconds.

Physical properties:

• Working time: 7 min.
• Start of hardening: 9 min.
• End of hardening: 13 min.
• Expansion (2 hours): 0.08%.
• Hardness (24 hours): 247 N/mm2.
• Crushing strength (1g): 58 N/mm2.

Packaging:

• 12Kg (6x2kg)

A combination of high-quality plastic and class IV gypsum, super hard, ideal for prosthetic works on implants. Peach colour.

Technical data:

• Working time 7 min.
• Start of hardening 8 min.
• End of hardening 10 min.
• Total hardening time 30 min.
• Expansion (2h): 0.10%.
• Compressive strength (1 h): 50 MP.
• powder to water ratio 100g/20ml.
• working temperature 20-23 degrees °C.
• mechanical mixing and vacuum 30sec.

Packaging:

• 12kg (6x2kg)

A combination of high-quality plastic and class IV plaster, super-hard, ideal for prosthetic work on implants.

Technical data:

• Grey colour.
• Working time 7 min.
• Start of hardening 8 min.
• End of hardening 10 minutes.
• Total hardening time 30 min.
• Expansion (2h): 0.10%.
• Compressive strength (1 h): 50 MP.
• powder to water ratio 100g/20ml.
• operating temperature 20-23 degrees °C.
• mechanical and vacuum mixing for 30 seconds.

Packaging:

• 12 kg (6x2kg)

High-quality synthetic modeling plaster. Perfect for all types of fixed dentures, residual limbs and master models.

Advantages:

• Releases from the impression precisely and easily (only 20 minutes!).
• Thixotropic.
• Very high durability.
• It allows you to obtain excellent results when working with optical scanning systems.

Instructions for use:

• Powder/water ratio: 100 g / 20 ml.
• Operating temperature: 20-23 °C.
• Mechanical mixing in vacuum: 30 seconds.
• Manual mixing: 60 seconds.

Physical properties:

• Working time: 8 min.
• Start of hardening: 10 min.
• End of hardening: 15 minutes.
• Expansion (2 hours): 0.08%.
• Hardness (24 hours): 268 N/mm2.
• Crushing strength (1g): 60 N/mm2.

Packaging:

• 12 kg (6x2kg)

Kromptypo 4. Class IV extra hard prosthetic plaster with chromatic setting phase indicator for making models with high compressive and abrasion resistance.

Characteristics:

• Final color: pastel yellow.
• Water to powder ratio: 22ml/100g.
• Absorption time: 20 seconds.
• Mixing time (manual): 60 seconds.
• Mixing time (mechanical): 30 seconds.
• Pouring time: 3 minutes.
• Setting time: 7 minutes.
• Separation time after setting: 25-30 minutes.
• Expansion setting (after 2 hours): 0.08%
• Compressive strength (after 24 hours): 81 MPa, 11,740 psi, 828 kg/cm2.
• Rockwell hardness (after 24 hours): 85 HRL.

Packaging:

• 25kg

Class IV plaster for model bases with excellent flow, orange color.

Advantages:

• Very liquid consistency.
• It does not require work with a vibrating table.
• No air bubbles between the pins.
• Low expansion.
• Absolutely smooth surface.
• High final hardness.
• Big time savings.

Physical properties:

• Setting time 10-12 minutes.
• Dry compressive strength 70 MPa.

Linear expansion:

• After 2 hours 0.06%

Preparation:

• Gypsum / distilled water: 100g / 23 ml.
• Operating temperature 23 °C.

Packaging:

• 25kg

Attention:

• Due to the heavy weight of the goods (25 kg), an additional fee will be added to the shipment.

Stodent III is a type 3 hard plaster recommended for antagonist models and working models when making removable and skeletal dentures.

Description:

• Light green color enriched with mango aroma.
• Small expansion.
• Good mechanical properties.

Advantages:

• Smooth surface.
• Easier model making thanks to high thixotropy.
• High resistance to fracture when released from the impression.

Technical data:

• Mixing proportions 30 ml / 100 g.
• Mixing time (vacuum) 30 s.
• Mixing time (manual) 60 – 90 s.
• Setting time 10 -14 min.
• Release time from the impression 45 min.
• Compressive resistance (after 1h ) 25 ± 2 MPa [> 20 MPa]
• Linear expansion (after 2 hours ) max. 0.15% [< 0.20 %]

Packaging:

• 25kg

Attention:

• Due to the heavy weight of the goods (25 kg), an additional fee will be added to the shipment.

Description:

• Stodent IV is a super-hard type 4 dental plaster recommended for making working models of fixed frame dentures and flexible dentures, combined works, and post-implantation dentures.
• Cream color with a vanilla scent
• Small expansion
• Liquidity

Advantages:

• Very good detail reproduction
• Smooth surface
• High resistance to mechanical damage

Technical data:

• Mixing proportions 20 ml / 100 g
• Mixing time (vacuum) 30 s
• Mixing time (manual) 60 – 90 s
• Setting time 8 -12 min.
• Compressive resistance (after 1h ) 45 ± 2 MPa [> 35 MPa]
• Linear expansion (after 2 hours ) max. 0.10% [< 0.15 %]
• Linear expansion after 24 hours < 0.18* %

Packaging:

• 25kg

Attention:

• Due to the heavy weight of the goods (25 kg), an additional fee will be added to the shipment.

Description:

• Stodent IV is a super-hard type 4 dental plaster recommended for making working models of fixed frame dentures and flexible dentures, combined works, and post-implantation dentures.
• Ash color with strawberry scent
• Small expansion
• Liquidity

Advantages:

• Very good detail reproduction
• Smooth surface
• High resistance to mechanical damage

Technical data:

• Mixing proportions 20 ml / 100 g
• Mixing time (vacuum) 30 s
• Mixing time (manual) 60 – 90 s
• Setting time 8 -12 min.
• Compressive resistance (after 1h ) 45 ± 2 MPa [> 35 MPa]
• Linear expansion (after 2 hours ) max. 0.10% [< 0.15 %]
• Linear expansion after 24 hours < 0.18* %

Packaging:

• 25kg

Attention:

• Due to the heavy weight of the goods (25 kg), an additional fee will be added to the shipment.