Vertex Self Curing polymer 500g

Vertex Self Curing is a self-curing acrylic resin.

Application:

• repair of dentures;
• performing denture relining;
• extending the range of partial and complete dentures.

Features:

• short polymerization time: the process takes only 10 minutes at a temperature of 45-55 °C at a pressure of 2.5 bar;
• ease of use: the material is easy to process and apply.

Available color variants:

• color 4: transparent,
• color 10: pink transparent with veins.

Packaging:

• 500g

Vertex Self Curing monomer 250ml

Vertex Self Curing.

Cold polymerization fluid.

Packaging:

• 250ml

Villacryl S set 100g/50ml

Villacryl S, a self-polymerizing material intended for denture repairs.

Colors:

• 0 colorless;
• V2 milky pink veined;
• V4 pink veined.

Characteristics:

• easy to prepare and process;
• enables quick repair of the prosthesis;
• guarantees the aesthetics of the repair;
• bonds well with the denture plate;
• does not contain heavy metals;
• biologically neutral.

Technical data:

• mixing proportions: 10 g powder / 5.3 ml (5 g);
• dough preparation time: 8 minutes;
• polymerization time: minimum 20 minutes at 50-60 °C, pressure 2 bar;
• fracture strength: > 60* MPa;
• solubility: < 8* µg/mm³;
• sorption: < 32* µg/mm³.

Packaging:

• 100g/50ml

FuturaSelf monomer 500ml

Futura Self, cold polymerization fluid.

Packaging:

• 500ml

Estetic S for repairs 100g/50ml

Estetic S self-polymerizing acrylic material for the repair of dentures and orthodontic appliances.

Available colors:

• 0 colorless;

• 8 pink unveined;

• 10 pink without veins;

• 8V pink with veins;

• 10V pink with veins;

Characteristics:

• for denture repairs;
• high quality material at a low price.

Technical data:

• mixing proportions: by weight powder/liquid - 2:1;
• dough preparation time: 2-5 minutes;
• Dough shelf life: 3.5 minutes;
• polymerization process: 20 min.; 40-50°C; 2 bar;
• residual monomer content: 3.46%;
• fracture strength: 62.5 Mpa;
• bending elasticity: 2043 MPa;
• solubility: 2.6 μg/mm³;
• sorption: 23.8 μg/mm³.

Packaging:

• 100g/50ml

Estetic S repair monomer 50ml

Estetic S, acrylic repair fluid.

Packaging:

• 50ml.

FuturaSelf Polymer pink transparent 1000g

FuturaSelf cold polymerizing acrylic material.

Colors:

• pink transparent veined.

Characteristics:

• for denture repairs;
• for denture relining.

Packaging:

• 1000g

Estetic S repair monomer 250ml

Estetic S denture repair fluid for cold polymerization.

Packaging:

• 250ml

Villacryl S monomer 200ml or 500ml

Villacryl S self-polymerizing fluid for denture repairs.

Packaging:

• 200ml or 500ml

Estetic S repair polymer 500g

Estetic S acrylic material intended for cold polymerization.

Characteristics:

• for repairing dentures;
• high quality material at a low price.

Technical data:

• mixing proportions: powder/liquid by weight - 2:1;
• dough preparation time: 2-5 minutes;
• Dough shelf life: 3.5 minutes;
• polymerization process: 20 min.; 40-50°C; 2 bar;
• residual monomer content: 3.46%;
• fracture strength: 62.5 Mpa;
• bending elasticity: 2043 MPa;
• solubility: 2.6 μg/mm3;
• sorption: 23.8 μg/mm3.

Available colors:

• 0 colorless;
• 8 pink without veins;
• 10 pink without veins;
• 8V pink with veins ;
• 10V pink with veins.

Packaging:

• 500 g

Villacryl S color V4 polymer 1000g

Villacryl S, a self-polymerizing material intended for denture repairs.

Characteristics:

• easy to prepare and process;
• enables quick repair of the prosthesis;
• guarantees the aesthetics of the repair;
• bonds well with the denture plate;
• does not contain heavy metals;
• biologically neutral;
• color V4 pink veined.

Packaging:

• 1000g

Vertex Self Curing color 10 polymer 1000g

Vertex Self Curing, self-polymerizing acrylic material.

Characteristics:

• color 10 pink transparent with veins;
• short polymerization time 10 min. at a temperature of 45-55 °C at a pressure of 2.5 bar;
• easy and convenient to use.

Application:

• denture repairs;
• denture relining;
• increasing the range of full and partial dentures.

Packaging:

• 1 pc.

Vertex Self Curing monomer 1000ml

Vertex Self Curing, cold polymerization fluid.

Packaging:

• 1000ml

Villacryl S polymer 1kg + monomer 500ml

Villacryl S, a self-polymerizing acrylic material intended for repairs and indirect relining of removable dentures.

Advantages:

• ease of preparation and processing;
• speed of execution thanks to good connection to hot polymerizing materials;
• the range of colors guarantees high aesthetics of the repair.

Technical data:

• mixing proportions 10 g powder / 5.3 ml (5 g);
• preparation time 8 minutes;
• polymerization process minimum 20 min.50-60 °C2 bar;
• fracture strength > 60* MPa;
• solubility < 8* µg/mm³;
• sorption < 32* µg/mm³.

Packaging:

• 1kg powder 500 ml liquid

Estetic S set 500g/250ml

Estetic S acrylic material intended for cold polymerization.

Characteristics:

• to perform repairs of dentures;
• high quality material at a low price.

Technical data:

• mixing proportions: by weight powder/liquid - 2:1;
• dough preparation time: 2-5 minutes;
• Dough shelf life: 3.5 minutes;
• polymerization process: 20 min.; 40-50°C; 2 bar;
• residual monomer content: 3.46%;
• fracture strength: 62.5 Mpa;
• bending elasticity: 2043 MPa;
• solubility: 2.6 μg/mm3;
• sorption: 23.8 μg/mm3.

Available colors:

• 0 colorless;

• 8 pink unveined;

• 10 pink without veins;

• 8V pink with veins;

• 10V pink with veins;

Packaging:

• 500g/250ml

Aplodent Cold set 100g + 50ml

Aplodent Cold is a cold polymerization acrylic material intended for the repair of removable full and partial dentures, acrylic parts of frame dentures and acrylic orthodontic appliances.

Colors:

• 0 – colorless;
• V26 – pink veined;
• V27 – milky pink veined;

Advantages:

• short waiting time to start work;
• fast polymerization only 10 minutes;
• the same color range as in Aplodent Hot guarantees high aesthetics of the repair;
• contains only organic pigments and is cadmium-free.

Technical data:

• mixing proportions: 10 g powder / 7 ml liquid;
• Dough shelf life: approx. 10 min. (at 23°C);
• polymerization time: minimum 10 min – 55°C 2 bar;
• fracture strength: > 60* MPa;
• solubility: < 8* µg/mm3;
• sorption: < 32* µg/mm3.

Packaging:

• 100g + 50ml